Device physics of thin-film polycrystalline cells and modules: Phase 1 annual report: February 1998--January 1999
This report describes work done by Colorado State University (CSU) during Phase 1 of this subcontract. CSU researchers continued to make basic measurements on CI(G)S and CdTe solar cells fabricated at different labs, to quantitatively deduce the loss mechanisms in these cells, and to make appropriate comparisons that illuminate where progress is being made. Cells evaluated included the new record CIGS cell, CIS cells made with and without CdS, and those made by electrodeposition and electroless growth from solution. Work on the role of impurities focused on sodium in CIS. Cells with varying amounts of sodium added during CIS deposition were fabricated at NREL using four types of substrates. The best performance was achieved with 10{sup {minus}2}--10{sup {minus}1} at% sodium, and the relative merits of proposed mechanisms for the sodium effect were compared. Researchers also worked on the construction and testing of a fine-focused laser-beam apparatus to measure local variations in polycrystalline cell performance. A 1{micro}m spot was achieved, spatial reproducibility in one and two dimensions is less than 1 {micro}m, and photocurrent is reliably measured when the 1{micro}m spot is reduced as low as 1-sun in intensity. In elevated-temperature stress tests, typical CdTe cells held at 100 C under illumination and normal resistive loads for extended periods of time were generally very stable; but those held under reverse or large forward bias and those contacted using larger amounts of copper were somewhat less stable. CdTe cell modeling produced reasonable fits to experimental data, including variations in back-contact barriers. A major challenge being addressed is the photovoltaic response of a single simple-geometry crystallite with realistic grain boundaries.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC36-99GO10337
- OSTI ID:
- 754640
- Report Number(s):
- NREL/SR-520-27663; TRN: AH200015%%7
- Resource Relation:
- Other Information: PBD: 21 Dec 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Device physics of thin-film polycrystalline cells and modules. Annual subcontract report, 6 December 1995--5 December 1996
Device Physics of Thin-Film Polycrystalline Cells and Modules; Final Subcontract Report; 6 December 1993-15 March 1998
Related Subjects
36 MATERIALS SCIENCE
PERFORMANCE TESTING
CADMIUM TELLURIDE SOLAR CELLS
COPPER SELENIDE SOLAR CELLS
INDIUM SELENIDE SOLAR CELLS
GALLIUM SELENIDES
PHOTOVOLTAICS
DEVICE PHYSICS
THIN-FILM POLYCRYSTALLINE
CELLS AND MODULES
CDTE
CIGS
ELECTRODEPOSITION
IMPURITIES
PERFORMANCE
STRESS TESTS
MODELING