Anti-reflection coatings on large area glass sheets. Final report, Motorola report No. 2366/4, DRD No. SE-5
Antireflective coatings which may be suitable for use on the covers of photovoltaic solar modules can be easily produced by a dipping process. The coatings are applied to glass by drawing sheets of glass vertically out of dilute aqueous sodium silicate solutions at a constant speed, allowing the adherent liquid film to dry, then exposing the dried film to concentrated sulfuric acid, followed by a water rinse and dry. The process produces coatings of good optical performance (96.7% peak transmission at 0.540 ..mu..M wavelength) combined with excellent stain and soil resistance, and good resistance to abrasion. The process is reproduceable and easily controlled.
- Research Organization:
- Motorola, Inc., Phoenix, AZ (USA). Semiconductor Group
- DOE Contract Number:
- NAS-7-100-955339
- OSTI ID:
- 7045485
- Report Number(s):
- DOE/JPL/955339-80/4
- Country of Publication:
- United States
- Language:
- English
Similar Records
Anti-reflection coatings on large area glass sheets. Quarterly technical report No. 3, July 1-September 30, 1979. Motorola report No. 2366/3. [For solar cell covers]
Anti-reflection coatings on large area glass sheets. Quarterly technical report No. 2, 1 April 1979-30 June 1979. Motorola report No. 2366/2
Anti-reflection coatings applied by acid-leaching process. Final report
Technical Report
·
Tue Jan 01 00:00:00 EST 1980
·
OSTI ID:7045485
Anti-reflection coatings on large area glass sheets. Quarterly technical report No. 2, 1 April 1979-30 June 1979. Motorola report No. 2366/2
Technical Report
·
Mon Jan 01 00:00:00 EST 1979
·
OSTI ID:7045485
Anti-reflection coatings applied by acid-leaching process. Final report
Technical Report
·
Mon Sep 01 00:00:00 EDT 1980
·
OSTI ID:7045485
Related Subjects
14 SOLAR ENERGY
ANTIREFLECTION COATINGS
FABRICATION
GLASS
SOLAR CELLS
AQUEOUS SOLUTIONS
CHEMICAL PREPARATION
COVERINGS
DIP COATING
DIPPED COATINGS
ETCHING
HUMIDITY
LIGHT TRANSMISSION
OPTICAL PROPERTIES
PERFORMANCE
SODIUM SILICATES
SOLAR CELL ARRAYS
SULFURIC ACID
WEATHERING
ALKALI METAL COMPOUNDS
COATINGS
DEPOSITION
DIRECT ENERGY CONVERTERS
DISPERSIONS
EQUIPMENT
HYDROGEN COMPOUNDS
INORGANIC ACIDS
MIXTURES
OXYGEN COMPOUNDS
PHOTOELECTRIC CELLS
PHOTOVOLTAIC CELLS
PHYSICAL PROPERTIES
SILICATES
SILICON COMPOUNDS
SODIUM COMPOUNDS
SOLAR EQUIPMENT
SOLUTIONS
SURFACE COATING
SURFACE FINISHING
SYNTHESIS
140501* - Solar Energy Conversion- Photovoltaic Conversion
ANTIREFLECTION COATINGS
FABRICATION
GLASS
SOLAR CELLS
AQUEOUS SOLUTIONS
CHEMICAL PREPARATION
COVERINGS
DIP COATING
DIPPED COATINGS
ETCHING
HUMIDITY
LIGHT TRANSMISSION
OPTICAL PROPERTIES
PERFORMANCE
SODIUM SILICATES
SOLAR CELL ARRAYS
SULFURIC ACID
WEATHERING
ALKALI METAL COMPOUNDS
COATINGS
DEPOSITION
DIRECT ENERGY CONVERTERS
DISPERSIONS
EQUIPMENT
HYDROGEN COMPOUNDS
INORGANIC ACIDS
MIXTURES
OXYGEN COMPOUNDS
PHOTOELECTRIC CELLS
PHOTOVOLTAIC CELLS
PHYSICAL PROPERTIES
SILICATES
SILICON COMPOUNDS
SODIUM COMPOUNDS
SOLAR EQUIPMENT
SOLUTIONS
SURFACE COATING
SURFACE FINISHING
SYNTHESIS
140501* - Solar Energy Conversion- Photovoltaic Conversion