Assessment of extent and degree of thermal damage to polymeric materials in the Three Mile Island Unit 2 reactor building. Volume VI
Thermal damage to susceptible materials in accessible regions shows damage-distribution patterns that indicate nonuniform intensity of exposure. No clear explanation for nonuniformity is found in existing evidence; e.g., in some regions a lack of thermally susceptible materials frustrates analysis. Elsewhere, burned materials are present next to materials that seem similar but appear unscathed - leading to conjecture that the latter materials preferentially absorb water vapor during periods of high local steam concentration. Most of the polar crane pendant shows heavy burns on one half of its circumferential surface. This evidence suggests that the polar crane pendant side that experienced heaviest burn damage was exposed to intense radiant energy from a transient fire plume in the reactor containment volume. Tests and simple heat-transfer calculations based on pressure and temperature records from the accident show that the atmosphere inside the reactor building was probably 8% hydrogen in air, a value not inconsistent with the extent of burn damage. Burn-pattern geography indicates uniform thermal exposure in the dome volume to the 406-ft level (about 6 ft below the polar crane girder), partial thermal exposure in the volume between the 406- and 347-ft levels as indicated by the polar crane cable, and lack of damage to most thermally susceptible materials in the west quadrant of the reactor building; some evidence of thermal exposure is seen in the free volume between the 305- and 347-ft levels.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC07-76ID01570
- OSTI ID:
- 5145952
- Report Number(s):
- GEND-INF-023-Vol.6; ON: DE84010031
- Country of Publication:
- United States
- Language:
- English
Similar Records
Assessment of extent and degree of thermal damage to polymeric materials in the Three Mile Island Unit 2 Reactor building
Assessment of thermal damage to polymeric materials by hydrogen deflagration in the Three Mile Island Unit 2 Reactor Building
Related Subjects
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS
THREE MILE ISLAND-2 REACTOR
COMBUSTION
FIRES
CRANES
DAMAGE
POLYMERS
REACTOR MATERIALS
CHEMICAL REACTIONS
ENRICHED URANIUM REACTORS
EQUIPMENT
MATERIALS
MATERIALS HANDLING EQUIPMENT
OXIDATION
POWER REACTORS
PWR TYPE REACTORS
REACTORS
THERMAL REACTORS
THERMOCHEMICAL PROCESSES
WATER COOLED REACTORS
WATER MODERATED REACTORS
220900* - Nuclear Reactor Technology- Reactor Safety
210200 - Power Reactors
Nonbreeding
Light-Water Moderated
Nonboiling Water Cooled