Through-Thickness Microstructure Characterization in a Centrifugally Cast Austenitic Stainless Steel Nuclear Reactor Primary Loop Pipe Using Time-of-Flight Neutron Diffraction
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States); New Mexico Institute of Mining and Technology, Socorro, NM (United States)
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Electric Power Research Inst. (EPRI), Charlotte, NC (United States); Georgia Institute of Technology, Atlanta, GA (United States)
The US code of Federal Regulations mandates regular inspection of centrifugally cast austenitic stainless steel pipe, commonly used in primary cooling loops in light-water nuclear power plants. These pipes typically have a wall thickness of ~8 cm. Unfortunately, inspection using conventional ultrasonic techniques is not reliable as the microstructure strongly attenuates ultrasonic waves. Work is ongoing to simulate the behavior of acoustic waves in this microstructure and ultimately develop an acoustic inspection method for reactor inspections. In order to account for elastic anisotropy in the material, the texture in the steel was measured as a function of radial distance though the pipe wall. Experiments were conducted on two 10 × 12.7 × 80 mm radial sections of a cast pipe using neutron diffraction scans of 2 mm slices using the HIPPO time-of-flight neutron diffractometer at the Los Alamos Neutron Science Center (LANSCE, Los Alamos, NM, USA). Strong textures dominated by a small number of austenite grains with their (100) direction aligned in the radial direction of the pipe were observed. ODF analysis indicated that up to 70% of the probed volume was occupied by just three single-grain orientations, consistent with grain sizes of almost 1 cm. Texture and phase fraction of both ferrite and austenite phases were measured along the length of the samples. These results will inform the development of a more robust diagnostic tool for regular inspection of this material.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA); USDOE Laboratory Directed Research and Development (LDRD) Program
- Grant/Contract Number:
- 89233218CNA000001
- OSTI ID:
- 1807857
- Alternate ID(s):
- OSTI ID: 1865003
- Report Number(s):
- LA-UR-21-26038; LA-UR-21-23057
- Journal Information:
- Quantum Beam Science, Vol. 5, Issue 2; ISSN 2412-382X
- Publisher:
- MDPICopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Spatially resolved texture and microstructure evolution of additively manufactured and gas gun deformed 304L stainless steel investigated by neutron diffraction and electron backscatter diffraction
EPICS Controlled Collimator for Controlling Beam Sizes in HIPPO