Effect of helium on irradiation creep behavior of B-doped F82H irradiated in HFIR
Journal Article
·
· Fusion Science and Technology
- Japan Atomic Energy Agency (JAEA), Rokkasho-mura (Japan)
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
The diameter of pressurized tubes of F82H and B-doped F82H irradiated up to similar to 6 dpa have been measured by a non-contacting laser profilometer. The irradiation creep strains of F82H irradiated at 573 and 673K were almost linearly dependent on the effective stress level for stresses below 260 MPa and 170 MPa, respectively. The creep strain of (BN)-B-10-F82H was similar to that of F82H IEA at each effective stress level except 294 MPa at 573K irradiation. For 673K irradiation, the creep strain of some (BN)-B-10-F82H tubes was larger than that of F82H tubes. However, the generation of similar to 300 appm He did not cause a large difference in the irradiation creep behavior at 6 dpa.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Fusion Energy Sciences (FES); Japan Atomic Energy Agency
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1336590
- Journal Information:
- Fusion Science and Technology, Vol. 68, Issue 3; ISSN 1536-1055
- Publisher:
- American Nuclear SocietyCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Cited by: 3 works
Citation information provided by
Web of Science
Web of Science
Similar Records
An F82H steel pressurized tube creep capsule for irradiation in HFIR
Ni-Doped F82H to Investigate He Effects in HFIR Irradiation
Irradiation hardening in F82H irradiated at 573 K in the HFIR
Journal Article
·
Tue May 01 00:00:00 EDT 2018
· Nuclear Materials and Energy
·
OSTI ID:1336590
+3 more
Ni-Doped F82H to Investigate He Effects in HFIR Irradiation
Journal Article
·
Tue Jul 15 00:00:00 EDT 2003
· Fusion Science and Technology
·
OSTI ID:1336590
+2 more
Irradiation hardening in F82H irradiated at 573 K in the HFIR
Journal Article
·
Sat Jan 01 00:00:00 EST 2011
· Journal of Nuclear Materials
·
OSTI ID:1336590
+4 more