Bio-hybrid integrated system for wide-spectrum solar energy harvesting
- The Univ. of New Mexico, Albuquerque, NM (United States)
- New Mexico State Univ., Las Cruces, NM (United States)
- Univ. of New Mexico, Albuquerque, NM (United States)
An integrated hybrid photovoltaic-thermoelectric system has been developed using multiple layers of organic photosensitizers on inorganic semiconductors in order to efficiently convert UV-visible and IR energy into electricity. The hot anode of n-type ZnO nanowires was fabricated using a thermal process on pre-seeded layer and results to be crystalline with a transmittance up to 92 % and a bandgap of 3.32 eV. The visible-UV light-active organic layer was deposited between the anode and cathode at room temperature using a layer-by-layer deposition onto ITO and ZnO and Bi2Te3 nanowires from aqueous solution. The organic layer, a cooperative binary ionic (CBI) solid is composed of oppositely charged porphyrin metal (Zn(II) and Sn(IV)(OH–)2) derivatives that are separately water soluble, but when combined form a virtually insoluble solid. The electron donor/acceptor properties (energy levels, band gaps) of the solid can be controlled by the choice of metals and the nature of the peripheral substituent groups of the porphyrin ring. The highly thermoelectric structure, which acts as a cold cathode, is composed of p-type Bi2Te3 nanowires with a thermoelectric efficiency (ZT) between ~0.7 to 1, values that are twice that expected for bulk Bi2Te3. Lastly, efficiency of the integrated device, was found to be 35 at 0.2 suns illumination and thermoelectric properties are enhanced by the charge transfer between the CBI and the Bi2Te3 is presented in terms of photo- and thermogenerated current and advantages of the low cost fabrication process is discussed.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- AC04-94AL85000
- OSTI ID:
- 1333866
- Report Number(s):
- SAND-2015-2631J; 581978
- Journal Information:
- Proceedings of SPIE - The International Society for Optical Engineering, Vol. 8983; ISSN 0277-786X
- Publisher:
- SPIECopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Catalyst-free growth of ZnO nanowires on ITO seed/glass by thermal evaporation method: Effects of ITO seed layer thickness
Mitigation of Electrical Failure of Silver Nanowires under Current Flow and the Application for Long Lifetime Organic Light-Emitting Diodes