Full elastic strain and stress tensor measurements from individual dislocation cells in copper through-Si vias
- National Institute of Standards and Technology, Gaithersburg, MD (United States)
- National Institute of Standard and Technology, Gaithersburg, MD (United States)
- Argonne National Lab. (ANL), Argonne, IL (United States)
We report non-destructive measurements of the full elastic strain and stress tensors from individual dislocation cells distributed along the full extent of a 50 mm-long polycrystalline copper via in Si is reported. Determining all of the components of these tensors from sub-micrometre regions within deformed metals presents considerable challenges. The primary issues are ensuring that different diffraction peaks originate from the same sample volume and that accurate determination is made of the peak positions from plastically deformed samples. For these measurements, three widely separated reflections were examined from selected, individual grains along the via. The lattice spacings and peak positions were measured for multiple dislocation cell interiors within each grain and the cell-interior peaks were sorted out using the measured included angles. A comprehensive uncertainty analysis using a Monte Carlo uncertainty algorithm provided uncertainties for the elastic strain tensor and stress tensor components.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1248965
- Journal Information:
- IUCrJ, Vol. 2, Issue 6; ISSN 2052-2525
- Publisher:
- International Union of CrystallographyCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Unexpected δ-Phase Formation in Additive-Manufactured Ni-Based Superalloy
|
journal | January 2016 |
Evaluation of intragranular strain and average dislocation density in single grains of a polycrystal using K-map scanning
|
journal | September 2016 |
Stress, strain and Raman shifts
|
journal | February 2019 |
High Resolution Mapping of Orientation and Strain Gradients in Metals by Synchrotron 3D X-ray Laue Microdiffraction
|
journal | March 2019 |
Similar Records
X-ray microbeam measurements of individual dislocation cell elastic strains in deformed single-crystal copper
Experimental Characterization of The Mesoscale Dislocation Density Tensor