Compaction of Titanium Powders
Accurate modeling of powder densification has been an area of active research for more than 60 years. The earliest efforts were focused on linearization of the data because computers were not readily available to assist with curve-fitting methods. In this work, eight different titanium powders (three different sizes of sponge fines<150 {micro}m,<75 {micro}m, and<45 {micro}m; two different sizes of a hydride-dehydride [HDH]<75 {micro}m and<45 {micro}m; an atomized powder; a commercially pure [CP] Ti powder from International Titanium Powder [ITP]; and a Ti 6 4 alloy powder) were cold pressed in a single-acting die instrumented to collect stress and deformation data during compaction. From these data, the density of each compact was calculated and then plotted as a function of pressure. The results show that densification of all the powders, regardless of particle size, shape, or chemistry, can be modeled accurately as the sum of an initial density plus the sum of a rearrangement term and a work-hardening term. These last two terms are found to be a function of applied pressure and take the form of an exponential rise.
- Research Organization:
- National Energy Technology Lab. (NETL), Pittsburgh, PA, and Morgantown, WV (United States). In-house Research; National Energy Technology Laboratory (NETL), Pittsburgh, PA, Morgantown, WV (United States)
- Sponsoring Organization:
- USDOE Office of Fossil Energy (FE)
- OSTI ID:
- 1037337
- Report Number(s):
- NETL-TPR-3417
- Journal Information:
- METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCEĀ , Vol. 42A, Issue 5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Sintering of sponge and hydride-dehydride titanium powders
Titanium Sheet Fabricated from Powder for Industrial Applications