DEVELOPMENT OF CRYSTALLINE CERAMICS FOR IMMOBILIZATION OF ADVANCED FUEL CYCLE REPROCESSING WASTES

Technical Report · Thu Sep 22 00:00:00 EDT 2011

DOI:https://doi.org/10.2172/1025517· OSTI ID:1025517

Fox, K; Brinkman, K

The Savannah River National Laboratory (SRNL) is developing crystalline ceramic waste forms to incorporate CS/LN/TM high Mo waste streams consisting of perovskite, hollandite, pyrochlore, zirconolite, and powellite phase assemblages. Simple raw materials, including Al{sub 2}O{sub 3}, CaO, and TiO{sub 2} were combined with simulated waste components to produce multiphase crystalline ceramics. Fiscal Year 2011 (FY11) activities included (i) expanding the compositional range by varying waste loading and fabrication of compositions rich in TiO{sub 2}, (ii) exploring the processing parameters of ceramics produced by the melt and crystallize process, (iii) synthesis and characterization of select individual phases of powellite and hollandite that are the target hosts for radionuclides of Mo, Cs, and Rb, and (iv) evaluating the durability and radiation stability of single and multi-phase ceramic waste forms. Two fabrication methods, including melting and crystallizing, and pressing and sintering, were used with the intent of studying phase evolution under various sintering conditions. An analysis of the XRD and SEM/EDS results indicates that the targeted crystalline phases of the FY11 compositions consisting of pyrochlore, perovskite, hollandite, zirconolite, and powellite were formed by both press and sinter and melt and crystallize processing methods. An evaluation of crystalline phase formation versus melt processing conditions revealed that hollandite, perovskite, zirconolite, and residual TiO{sub 2} phases formed regardless of cooling rate, demonstrating the robust nature of this process for crystalline phase development. The multiphase ceramic composition CSLNTM-06 demonstrated good resistance to proton beam irradiation. Electron irradiation studies on the single phase CaMoO{sub 4} (a component of the multiphase waste form) suggested that this material exhibits stability to 1000 years at anticipated self-irradiation doses (2 x 10{sup 10}-2 x 10{sup 11} Gy), but that its stability may be rate dependent, therefore limiting the activity of the waste for which it can be employed. Overall, these preliminary results indicate good radiation damage tolerance for the crystalline ceramic materials. The PCT results showed that, for all of the waste forms tested, the normalized release values for most of the elements measured, including all of the lanthanides and noble metals, were either very small or below the instrument detection limits. Elevated normalized release values were measured only for Cs, Mo, and Rb. It is difficult to draw further conclusions from these data until a benchmark material is developed for the PCT with this type of waste form. Calcined, simulated CS/LN/TM High Mo waste without additives had relatively low normalized release values for Cs, Mo, and Rb. A review of the chemical composition data for this sample showed that these elements were well retained after the calcination. Therefore, it will be useful to further characterize the calcined material to determine what form these elements are in after calcining. This, along with single phase studies on Cs containing crystal structures such as hollandite, should provide insight into the most ideal phases to incorporate these elements to produce a durable waste form.

• Research Organization: Savannah River Site (SRS), Aiken, SC (United States)
• Sponsoring Organization: USDOE
• DOE Contract Number: DE-AC09-08SR22470
• OSTI ID: 1025517
• Report Number(s): SRNL-STI-2011-00516; TRN: US1104981
• Country of Publication: United States
• Language: English

Related Subjects

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS
12 MANAGEMENT OF RADIOACTIVE WASTES, AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS
CERAMICS
CHEMICAL COMPOSITION
CRYSTAL STRUCTURE
FUEL CYCLE
HOLLANDITE
IRRADIATION
PEROVSKITE
PHASE STUDIES
PROCESSING
PROTON BEAMS
PYROCHLORE
RADIOISOTOPES
RARE EARTHS
RAW MATERIALS
REPROCESSING
SINTERING
STABILITY
SYNTHESIS
WASTE FORMS
WASTES
X-RAY DIFFRACTION
ZIRCONOLITE