Phase equilibria in W-Fe-Co-Ni system alloys I. Alloys containing 10% (Fe+Co+Ni) at 1400-1200/sup 0/ C
The authors investigate the phase composition of W-Fe-Co-Ni system alloys with a total (Fe + Co + Ni) content of 10% at 1400-1200 C and also of their solidus temperature. The alloys were prepared from powders of tungsten (not less than 99.87% ), carbonyl nickel (not less than 99.98%), type ChDA iron (not less than 99.55%), and cobalt (not less than 99.5%) with a particle size of 1.7-70 um. The phase composition of the alloys was studied by methods of metallographic, x-ray, and micro-x-ray spectral analysis and also by measurement of the microhardness of the coexisting phases. upon Completiodnof crystallization and at temperatures of 1400-1200 C alloys of the primary section with 10% (Fe + Co + Ni) have a two-(alpha + u or alpha + gamma) or three phase (alpha + u + gamma) structure.
- Research Organization:
- Moscow Institute for Steele and Alloys
- OSTI ID:
- 6874000
- Journal Information:
- Sov. Powder Metall. Met. Ceram. (Engl. Transl.); (United States), Vol. 25:4
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of thermal aging on the mechanical properties of Ni--Cr--Mo--Fe alloy. [At 1000/sup 0/, 1200/sup 0/, 1400/sup 0/ and 1600/sup 0/F]
Effects of Cr/Ni ratio on physical properties of Cr-Mn-Fe-Co-Ni high-entropy alloys
Related Subjects
COBALT ALLOYS
MICROSTRUCTURE
PHASE STUDIES
IRON ALLOYS
NICKEL ALLOYS
TUNGSTEN BASE ALLOYS
CRYSTALLIZATION
EQUILIBRIUM
METALLOGRAPHY
PHASE DIAGRAMS
POWDER METALLURGY
PRESSURE EFFECTS
QUANTITY RATIO
TEMPERATURE EFFECTS
X-RAY DIFFRACTION
ALLOYS
COHERENT SCATTERING
CRYSTAL STRUCTURE
DIAGRAMS
DIFFRACTION
METALLURGY
PHASE TRANSFORMATIONS
SCATTERING
TUNGSTEN ALLOYS
360102* - Metals & Alloys- Structure & Phase Studies