100 MeV O{sup 7+} irradiation induced red shift in the band gaps of 3 wt% 'Li' doped Nb{sub 2}O{sub 5} thin film
Journal Article
·
· AIP Conference Proceedings
- Department of Physics, Presidency College, Chennai - 600005 (India)
- Center for Condensed Matter Sciences, National Taiwan University, Taipei - 10617, Taiwan (China)
- Department of Nuclear Physics, University of Madras, Guindy Campus, Chennai - 600025 (India)
- Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India)
- Interuniversity Accelerator Centre, Aruna Asaf Ali Marg, New Delhi, 110067 (India)
Nb{sub 2}O{sub 5}:Li (3 wt%) thin film of thickness 353 nm spray deposited onto ITO coated glass substrate at 350 °C is irradiated with 100 MeV O{sup 7+} ion at a fluence of 5×10{sup 12} ions/cm{sup 2}. X-ray diffraction shows that the pristine and irradiated films are polycrystalline with a tetragonal phase. Raman peaks suppressed upon irradiation imply large surface degradation which is also seen as a decrement in transparency in visible region to one half of the pristine film. Large red shift is observed in direct and indirect band gaps upon irradiation. Hall effect reveals slight increase in carrier concentration due to irradiation induced defects.
- OSTI ID:
- 22271054
- Journal Information:
- AIP Conference Proceedings, Vol. 1591, Issue 1; Conference: 58. DAE solid state physics symposium 2013, Patiala, Punjab (India), 17-21 Dec 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
200 MeV Ag{sup 15+} ion beam irradiation effects on spray deposited 5 wt% 'Li' doped V{sub 2}O{sub 5} thin film
Improved optical and electrical properties of 200 MeV Ag{sup 15+} irradiated 3 wt% 'Li' doped MoO{sub 3} thin film
Structural, optical and transport properties of 100 MeV oxygen ion irradiated V{sub 2}O{sub 5} thin film
Journal Article
·
Mon May 23 00:00:00 EDT 2016
· AIP Conference Proceedings
·
OSTI ID:22271054
+2 more
Improved optical and electrical properties of 200 MeV Ag{sup 15+} irradiated 3 wt% 'Li' doped MoO{sub 3} thin film
Journal Article
·
Tue Feb 05 00:00:00 EST 2013
· AIP Conference Proceedings
·
OSTI ID:22271054
+5 more
Structural, optical and transport properties of 100 MeV oxygen ion irradiated V{sub 2}O{sub 5} thin film
Journal Article
·
Tue Jun 05 00:00:00 EDT 2012
· AIP Conference Proceedings
·
OSTI ID:22271054
+4 more
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CONCENTRATION RATIO
DOPED MATERIALS
HALL EFFECT
ION BEAMS
IRRADIATION
LITHIUM COMPOUNDS
MEV RANGE
MULTICHARGED IONS
NIOBIUM OXIDES
OXYGEN IONS
PHYSICAL RADIATION EFFECTS
POLYCRYSTALS
RAMAN SPECTROSCOPY
RED SHIFT
SUBSTRATES
SURFACES
THIN FILMS
X-RAY DIFFRACTION
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CONCENTRATION RATIO
DOPED MATERIALS
HALL EFFECT
ION BEAMS
IRRADIATION
LITHIUM COMPOUNDS
MEV RANGE
MULTICHARGED IONS
NIOBIUM OXIDES
OXYGEN IONS
PHYSICAL RADIATION EFFECTS
POLYCRYSTALS
RAMAN SPECTROSCOPY
RED SHIFT
SUBSTRATES
SURFACES
THIN FILMS
X-RAY DIFFRACTION