Temperature-dependent mechanical property testing of nitrate thermal storage salts.
Three salt compositions for potential use in trough-based solar collectors were tested to determine their mechanical properties as a function of temperature. The mechanical properties determined were unconfined compressive strength, Young's modulus, Poisson's ratio, and indirect tensile strength. Seventeen uniaxial compression and indirect tension tests were completed. It was found that as test temperature increases, unconfined compressive strength and Young's modulus decreased for all salt types. Empirical relationships were developed quantifying the aforementioned behaviors. Poisson's ratio tends to increase with increasing temperature except for one salt type where there is no obvious trend. The variability in measured indirect tensile strength is large, but not atypical for this index test. The average tensile strength for all salt types tested is substantially higher than the upper range of tensile strengths for naturally occurring rock salts. Interest in raising the operating temperature of concentrating solar technologies and the incorporation of thermal storage has motivated studies on the implementation of molten salt as the system working fluid. Recently, salt has been considered for use in trough-based solar collectors and has been shown to offer a reduction in levelized cost of energy as well as increasing availability (Kearney et al., 2003). Concerns regarding the use of molten salt are often related to issues with salt solidification and recovery from freeze events. Differences among salts used for convective heat transfer and storage are typically designated by a comparison of thermal properties. However, the potential for a freeze event necessitates an understanding of salt mechanical properties in order to characterize and mitigate possible detrimental effects. This includes stress imparted by the expanding salt. Samples of solar salt, HITEC salt (Coastal Chemical Co.), and a low melting point quaternary salt were cast for characterization tests to determine unconfined compressive strength, indirect tensile strength, coefficient of thermal expansion (CTE), Young's modulus, and Poisson's ratio. Experiments were conducted at multiple temperatures below the melting point to determine temperature dependence.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 991535
- Report Number(s):
- SAND2010-6013; TRN: US201021%%278
- Country of Publication:
- United States
- Language:
- English
Similar Records
Technical Performance of Refractory Liners for Molten Chloride Salt Thermal Energy Storage Systems
Material Property Determinations for Alluvium in Support of Source Physics Experiment
Related Subjects
25 ENERGY STORAGE
AVAILABILITY
COMPRESSION
HEAT STORAGE
HEAT TRANSFER
IMPLEMENTATION
MECHANICAL PROPERTIES
MELTING POINTS
MOLTEN SALTS
NITRATES
SALT DEPOSITS
SOLAR COLLECTORS
SOLIDIFICATION
STORAGE
TEMPERATURE DEPENDENCE
TENSILE PROPERTIES
TESTING
THERMAL EXPANSION
THERMODYNAMIC PROPERTIES
WORKING FLUIDS
Rock salt-Thermomechanical properties.