Thermite combustion enhancement resulting from biomodal luminum distribution
- Kevin M.
- Michelle
- Steven F.
In recent years many studies that incorporated nano-scale or ultrafine aluminum (Al) as part of an energetic formulation and demonstrated significant performance enhancement. Decreasing the fuel particle size from the micron to nanometer range alters the material's chemical and thermal-physical properties. The result is increased particle reactivity that translates to an increase in the combustion wave speed and ignition sensitivity. Little is known, however, about the critical level of nano-sized fuel particles needed to enhance the performance of the energetic composite. Ignition sensitivity and combustion wave speed experiments were performed using a thermite composite of Al and MoO{sub 3} pressed to a theoretical maximum density of 50% (2 g/cm{sup 3}). A bimodal Al particle size distribution was prepared using 4 or 20 {mu}m Al fuel particles that were replaced in 10% increments by 80 nm Al particles until the fuel was 100% 80 nm Al. These bimodal distributions allow the unique characteristics of nano-scale materials to be better understood. The pellets were ignited using a 50W CO{sub 2} laser. High speed imaging diagnostics were used to measure the ignition delay time and combustion wave speed.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 977627
- Report Number(s):
- LA-UR-04-2949; TRN: US1003651
- Resource Relation:
- Conference: Submitted to 31st International Pyrotechnics Seminar, Fort Collins, CO, July 11-16, 2004
- Country of Publication:
- United States
- Language:
- English
Similar Records
Propagation studies of metastable intermolecular composites (MIC).
Ignition dynamics and activation energies of metallic thermites: From nano- to micron-scale particulate composites