Title: Double patterning HSQ processes of zone plates for 10 nm diffraction limitedperformance

Abstract

In e-beam lithography, fabrication of sub-20 nm dense structures is challenging. While there is a constant effort to develop higher resolution resist processes, the progress of increasing pattern density is slow. For zone plates, consisting of dense lines and spaces, the outermost zone width has been limited to slightly less than 20 nm due to effects such as low aerial image contrast, forward scattering, intrinsic resist resolution, and development issues. To circumvent these effects, we have successfully developed a new double patterning HSQ process, and as a result, we have fabricated zone plates of 10 and 12 nm using the process. We previously developed a double patterning process in which a dense zone plate pattern is sub-divided into two semi-isolated, complementary zone set patterns. These patterns are fabricated separately and then overlaid with high accuracy to yield the desired pattern. The key to success with this process is the accuracy of the overlay. For diffraction-limited zone plates, accuracy better than one-third of the smallest zone width is needed. In our previous work, the zone set patterns were formed using PMMA and gold electroplating, which were overlaid and aligned to the zero-level mark layer with sub-pixel accuracy using our internally developedmore » algorithm. The complete zone plate fabrication was conducted in-house. With this process, we successfully fabricated zone plates of 15 nm outermost zone. Using this zone plate, we were able to achieve sub-15 nm resolution at 1.52 nm wavelength, the highest resolution ever demonstrated in optical microscopy at that time. We attempted to extend the process to fabricating 12 nm and smaller zones. However, the modest PMMA contrast, combined with a relatively large electron beam size compared to the target feature sized limited the process latitude. To overcome this problem, we developed a new overlay process based on high resolution negative tone resist of hydrogen silsesquioxane (HSQ). With the development in TMAH at 45 C, we can reliably achieve zone width as small as 8 nm with negligible line edge roughness in the semi-dense zone set. Such narrow zones in HSQ, however, detach easily from the gold plating base substrate needed for the electroplating step. We developed a process to condition the gold substrate with (3-mercaptopropyl) trimethoxysilane, or 3-MTP, which can form a homogeneous hydroxylation surface on gold surface and bond with hydroxyl in HSQ. Fig 2 shows the basic process steps of the double patterning HSQ process. Unlike the PMMA process, both zone sets are formed in HSQ and overlaid, and the complete zone plate pattern is converted to gold using electroplating in the final step. Using the new process, we successfully realized zone plates of 10 nm and 12 nm outermost zones. Fig. 3 shows the SEM micrographs of the zone plates outer regions. The zone plates are 30 nm thick in gold. To the best of our knowledge, these zone plates have the smallest zonal features ever fabricated using e-beam lithography. The complete zone plate fabrication was conducted in-house, using our vector scan electron beam lithography tool, the Nanowriter, which has a measured beam diameter of 6.5 nm (FWHM) at 100 keV. An internally developed, sub-pixel alignment algorithm, based on auto/cross-correlation methods, was used for the overlay. A 12 nm zone plate was tested with a full-field transmission x-ray microscope at the LBNL's Advanced Light Source. Fig. 4 shows an x-ray image of a 40 nm thick gold radial spoke pattern taken with the zone plate at 1.75 nm wavelength (707eV, FeL3 edge), along with the scanning transmission electron micrograph of same object. Numerous small features in the object can be seen in the x-ray image. Data analysis indicates that a near diffraction limited performance was achieved using the zone plate. In our presentation, we will discuss the details and subtleties of the overlay fabrication as well as the zone plate image results.« less

Authors:
; ; ; ; ;
Publication Date:
Research Org.:
Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
Sponsoring Org.:
Materials Sciences Division
OSTI Identifier:
959418
Report Number(s):
LBNL-1396E-Ext-Abs
TRN: US0904767
DOE Contract Number:  
DE-AC02-05CH11231
Resource Type:
Conference
Resource Relation:
Conference: The 53rd International Symposium on Electron, Ion, and Photon Beams and Nanolithography, Marco Island, FL, May 26-29, 2009
Country of Publication:
United States
Language:
English
Subject:
36; ACCURACY; ADVANCED LIGHT SOURCE; DATA ANALYSIS; DIFFRACTION; ELECTRON BEAMS; ELECTRONS; ELECTROPLATING; FABRICATION; GOLD; OPTICAL MICROSCOPY; PERFORMANCE; PHOTON BEAMS; PLATES; RESOLUTION

Citation Formats

Chao, Weilun, Kim, Jihoon, Anderson, Erik H, Fischer, Peter, Rekawa, Senajith, and Attwood, David T. Double patterning HSQ processes of zone plates for 10 nm diffraction limitedperformance. United States: N. p., 2009. Web.
Chao, Weilun, Kim, Jihoon, Anderson, Erik H, Fischer, Peter, Rekawa, Senajith, & Attwood, David T. Double patterning HSQ processes of zone plates for 10 nm diffraction limitedperformance. United States.
Chao, Weilun, Kim, Jihoon, Anderson, Erik H, Fischer, Peter, Rekawa, Senajith, and Attwood, David T. 2009. "Double patterning HSQ processes of zone plates for 10 nm diffraction limitedperformance". United States. https://www.osti.gov/servlets/purl/959418.
@article{osti_959418,
title = {Double patterning HSQ processes of zone plates for 10 nm diffraction limitedperformance},
author = {Chao, Weilun and Kim, Jihoon and Anderson, Erik H and Fischer, Peter and Rekawa, Senajith and Attwood, David T},
abstractNote = {In e-beam lithography, fabrication of sub-20 nm dense structures is challenging. While there is a constant effort to develop higher resolution resist processes, the progress of increasing pattern density is slow. For zone plates, consisting of dense lines and spaces, the outermost zone width has been limited to slightly less than 20 nm due to effects such as low aerial image contrast, forward scattering, intrinsic resist resolution, and development issues. To circumvent these effects, we have successfully developed a new double patterning HSQ process, and as a result, we have fabricated zone plates of 10 and 12 nm using the process. We previously developed a double patterning process in which a dense zone plate pattern is sub-divided into two semi-isolated, complementary zone set patterns. These patterns are fabricated separately and then overlaid with high accuracy to yield the desired pattern. The key to success with this process is the accuracy of the overlay. For diffraction-limited zone plates, accuracy better than one-third of the smallest zone width is needed. In our previous work, the zone set patterns were formed using PMMA and gold electroplating, which were overlaid and aligned to the zero-level mark layer with sub-pixel accuracy using our internally developed algorithm. The complete zone plate fabrication was conducted in-house. With this process, we successfully fabricated zone plates of 15 nm outermost zone. Using this zone plate, we were able to achieve sub-15 nm resolution at 1.52 nm wavelength, the highest resolution ever demonstrated in optical microscopy at that time. We attempted to extend the process to fabricating 12 nm and smaller zones. However, the modest PMMA contrast, combined with a relatively large electron beam size compared to the target feature sized limited the process latitude. To overcome this problem, we developed a new overlay process based on high resolution negative tone resist of hydrogen silsesquioxane (HSQ). With the development in TMAH at 45 C, we can reliably achieve zone width as small as 8 nm with negligible line edge roughness in the semi-dense zone set. Such narrow zones in HSQ, however, detach easily from the gold plating base substrate needed for the electroplating step. We developed a process to condition the gold substrate with (3-mercaptopropyl) trimethoxysilane, or 3-MTP, which can form a homogeneous hydroxylation surface on gold surface and bond with hydroxyl in HSQ. Fig 2 shows the basic process steps of the double patterning HSQ process. Unlike the PMMA process, both zone sets are formed in HSQ and overlaid, and the complete zone plate pattern is converted to gold using electroplating in the final step. Using the new process, we successfully realized zone plates of 10 nm and 12 nm outermost zones. Fig. 3 shows the SEM micrographs of the zone plates outer regions. The zone plates are 30 nm thick in gold. To the best of our knowledge, these zone plates have the smallest zonal features ever fabricated using e-beam lithography. The complete zone plate fabrication was conducted in-house, using our vector scan electron beam lithography tool, the Nanowriter, which has a measured beam diameter of 6.5 nm (FWHM) at 100 keV. An internally developed, sub-pixel alignment algorithm, based on auto/cross-correlation methods, was used for the overlay. A 12 nm zone plate was tested with a full-field transmission x-ray microscope at the LBNL's Advanced Light Source. Fig. 4 shows an x-ray image of a 40 nm thick gold radial spoke pattern taken with the zone plate at 1.75 nm wavelength (707eV, FeL3 edge), along with the scanning transmission electron micrograph of same object. Numerous small features in the object can be seen in the x-ray image. Data analysis indicates that a near diffraction limited performance was achieved using the zone plate. In our presentation, we will discuss the details and subtleties of the overlay fabrication as well as the zone plate image results.},
doi = {},
url = {https://www.osti.gov/biblio/959418}, journal = {},
number = ,
volume = ,
place = {United States},
year = {Fri Jan 09 00:00:00 EST 2009},
month = {Fri Jan 09 00:00:00 EST 2009}
}

Conference:
Other availability
Please see Document Availability for additional information on obtaining the full-text document. Library patrons may search WorldCat to identify libraries that hold this conference proceeding.

Save / Share: