Evaluating the Relationship between Slabbing of Cr2O3/MgO Refractories Used in Steelmaking and Spalling of High Chrome Oxide Refractories Used in Gasification
Because of its excellent corrosion resistance and high temperature properties, chrome oxide refractories have been used in a number of severe service environments, including steelmaking and gasification. Refractory failure of Cr2O3/MgO or MgO/Cr2O3 refractories in steelmaking can involve a phenomena called slabbing, peeling, or chemical spalling. A similar failure mechanism exists in the high chrome oxide materials used in gasification. Gasifiers contain the reaction between a carbon feedstock, water, and oxygen under reducing conditions; producing H2 and CO used in chemicals or as fuel for power plants. A slagging gasifier typically operates between 1250- 1575°C, and with pressures between 300-1000 psi. Gasification refractory failure is by chemical dissolution and/or by spalling. Spalling is caused by slag penetration of the porous refractory surface and by expansion differences between the penetrated/non-penetrated areas, and is exacerbated by thermal cycling. Similarities between slabbing of steelmaking refractories and spalling of gasification refractories will be discussed.
- Research Organization:
- National Energy Technology Laboratory (NETL), Pittsburgh, PA, Morgantown, WV, and Albany, OR (United States)
- Sponsoring Organization:
- USDOE - Office of Fossil Energy (FE)
- DOE Contract Number:
- None cited
- OSTI ID:
- 913313
- Report Number(s):
- DOE/NETL-IR-2007-220; TRN: US200802%%763
- Resource Relation:
- Conference: Materials Science & Technology (MS&T06), Cincinnati OH, Oct. 15-19, 2006
- Country of Publication:
- United States
- Language:
- English
Similar Records
Field Trial Results of an Improved Refractory Material for Slagging Gasifiers
Refractory failure in slagging gasifiers