Control of Urania Crystallite Size by HMTA-Urea Reactions in the Internal Gelation Process for Preparing (U, Pu)O2Fuel Kernels
In the development of (U,Pu)O{sub 2} kernels by the internal gelation process for the Direct Press Spheroidized process at Oak Ridge National Laboratory, a novel crystal growth step was discovered that made it possible to prepare calcined porous kernels that could be used as direct-press feed for Fast Breeder Reactor pellet fabrication. High-quality pellets were prepared that were near theoretical density and that (upon examination) revealed no evidence of sphere remnants. The controlled crystal growth step involved using hexamethylenetetramine (HMTA)-urea stock solutions that were boiled for 60 min or less. Before this discovery, all the other crystal growth steps (when utilized) could reduce the tap density to only {approx}1.3 g/cm{sup 3}, which was not sufficiently low for use in ideal pellet pressing. The use of the boiled HMTA-urea solution allowed the tap density to be lowered to 0.93 g/cm{sup 3}, with the ideal density being about 1.0 g/cm{sup 3}. This report describes the development of this technology and its scaleup.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 885943
- Report Number(s):
- ORNL/TM-2005/10; TRN: US0604117
- Country of Publication:
- United States
- Language:
- English
Similar Records
Key properties of mixed cerium and zirconium microspheres prepared by the internal gelation process with previously boiled HMTA and urea
Chemical flowsheet conditions for preparing urania spheres by internal gelation