Pre-treatment for molybdenum or molybdenum-rich alloy articles to be plated
Patent
·
OSTI ID:863613
- Oak Ridge, TN
This invention is a method for etching a molybdenum or molybdenum-rich alloy surface to promote the formation of an adherent bond with a subsequently deposited metallic plating. In a typical application, the method is used as a pre-treatment for surfaces to be electrolessly plated with nickel. The pre-treatment comprises exposing the crystal boundaries of the surface by (a) anodizing the surface in acidic solution to form a continuous film of gray molybdenum oxide thereon and (b) removing the film.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- W-7405-ENG-26
- Assignee:
- United States of America as represented by United States (Washington, DC)
- Patent Number(s):
- US 4212907
- OSTI ID:
- 863613
- Country of Publication:
- United States
- Language:
- English
Similar Records
Pre-treatment for molybdenum or molybdenum-rich alloy articles to be plated
Pre-treatment for molybdenum or molybdenum-rich alloy articles to be plated
Aspects of electroless nickel plating on molybdenum
Patent
·
Tue Jul 15 00:00:00 EDT 1980
·
OSTI ID:863613
Pre-treatment for molybdenum or molybdenum-rich alloy articles to be plated
Patent
·
Tue Jul 15 00:00:00 EDT 1980
·
OSTI ID:863613
Aspects of electroless nickel plating on molybdenum
Conference
·
Sun Jul 01 00:00:00 EDT 1984
·
OSTI ID:863613
+2 more
Related Subjects
pre-treatment
molybdenum
molybdenum-rich
alloy
articles
plated
method
etching
surface
promote
formation
adherent
bond
subsequently
deposited
metallic
plating
typical
application
surfaces
electrolessly
nickel
comprises
exposing
crystal
boundaries
anodizing
acidic
solution
form
continuous
film
gray
oxide
thereon
removing
typical application
alloy surface
acidic solution
molybdenum oxide
subsequently deposited
comprises exposing
alloy articles
molybdenum-rich alloy
electrolessly plated
alloy article
subsequently deposit
continuous film
/427/205/428/
molybdenum
molybdenum-rich
alloy
articles
plated
method
etching
surface
promote
formation
adherent
bond
subsequently
deposited
metallic
plating
typical
application
surfaces
electrolessly
nickel
comprises
exposing
crystal
boundaries
anodizing
acidic
solution
form
continuous
film
gray
oxide
thereon
removing
typical application
alloy surface
acidic solution
molybdenum oxide
subsequently deposited
comprises exposing
alloy articles
molybdenum-rich alloy
electrolessly plated
alloy article
subsequently deposit
continuous film
/427/205/428/