Redox Bias in Loss on Ignition Moisture Measurement for Relatively Pure Plutonium-Bearing Oxide Materials
This paper evaluates potential analytical bias in application of the Loss on Ignition (LOI) technique for moisture measurement to relatively pure (plutonium assay of 80 wt.% or higher) oxides containing uranium that have been stabilized according to stabilization and storage standard DOE-STD-3013-2000 (STD- 3013). An immediate application is to Rocky Flats (RF) materials derived from high-grade metal hydriding separations subsequently treated by multiple calcination cycles. Specifically evaluated are weight changes due to oxidation/reduction of multivalent impurity oxides that could mask true moisture equivalent content measurement. Process knowledge and characterization of materials representing complex-wide materials to be stabilized and packaged according to STD-3013, and particularly for the immediate RF target stream, indicate that oxides of uranium, iron and gallium are the only potential multivalent constituents expected to be present above 0.5 wt.%. The evaluation show s that of these constituents, with few exceptions, only uranium oxides can be present at a sufficient level to produce weight gain biases significant with respect to the LOI stability test. In general, these formerly high-value, high-actinide content materials are reliably identifiable by process knowledge and measurement. Significant bias also requires that UO2 components remain largely unoxidized after calcination and are largely converted to U3O8 during LOI testing at only slightly higher temperatures. Based on well-established literature, it is judged unlikely that this set of conditions will be realized in practice. We conclude that it is very likely that LOI weight gain bias will be small for the immediate target RF oxide materials containing greater than 80 wt.% plutonium plus a much smaller uranium content. Recommended tests are in progress to confirm these expectations and to provide a more authoritative basis for bounding LOI oxidation/reduction biases. LOI bias evaluation is more difficult for lower purity materials and for fuel-type uranium-plutonium oxides. However, even in these cases testing may show that bias effects are manageable.
- Research Organization:
- Los Alamos National Laboratory Los Alamos, New Mexico (US); U. S. Department of Energy Rocky Flats Environmental Technology Site Golden, Colorado; Fluor Hanford Company Richland, Washington (US)
- Sponsoring Organization:
- US Department of Energy (US)
- OSTI ID:
- 834049
- Resource Relation:
- Conference: Waste Management 2002 Symposium, Tucson, AZ (US), 02/24/2002--02/28/2002; Other Information: PBD: 26 Feb 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
TECHNICAL BASIS FOR DOE STANDARD 3013 EQUIVALENCY SUPPORTING REDUCED TEMPERATURE STABILIZATION OF OXALATE-DERIVED PLUTONIUM OXIDE PRODUCED BY THE HB-LINE FACILITY AT SAVANNAH RIVER SITE
Materials identification and surveillance project item evaluation: Items, impure plutonium oxide (ATL27960) and pure plutonium oxide (PEOR3258)