Measuring the Fracture Toughness of TZM and ODS Molybdenum Alloys Using Standard and Sub-Sized Bend Specimens
Oxide Dispersion Strengthened (ODS) and TZM molybdenum have excellent creep resistance and strength at high temperatures in inert atmospheres. Fracture toughness and tensile testing was performed at temperatures between -150 degrees C and 450 degrees C to characterize 6.35 mm thick plate material of ODS and TZM molybdenum. A transition from low fracture toughness values (5.8 to 29.6 MPa square root m) to values greater than 30 MPa square root m is observed for TZM molybdenum in the longitudinal orientation at 100 degrees C and in the transverse orientation at 150 degrees C. These results are consistent with data reported in literature for molybdenum. A transition to low fracture toughness values (less than 30 MPa square root m) was not observed for longitudinal ODS molybdenum at temperatures greater than or equal to -150 degrees C, while a transition to low fracture toughness values (12.6 to 25.4 MPa square root m) was observed for the transverse orientation at room-temperature. The fi ne spacing of La-oxide precipitates that are present in ODS molybdenum result in a transition temperature that is significantly lower than any molybdenum alloy reported to date, with upper bound fracture toughness values that bound the literature data. A comparison of fracture toughness values obtained using a 1T, 0.5T, and 0.25T Charpy shows that a 0.5T Charpy could be used as a sub-sized specimen geometry.
- Research Organization:
- Bettis Atomic Power Lab., West Mifflin, PA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC11-98PN38206
- OSTI ID:
- 807260
- Report Number(s):
- B-T-3387; TRN: US200411%%633
- Resource Relation:
- Other Information: Supercedes report DE00807260; PBD: 1 Dec 2002; PBD: 1 Dec 2002
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-situ Fracture Studies and Modeling of the Toughening Mechanism Present in Wrought LCAC, TZM, and ODS Molybdenum Flat Products
Post-Irradiation Fracture Toughness of Unalloyed Molybdenum, ODS molybdenum, and TZM molybdenum following irradiation at 244C to 507C