Title: Occurrence, Characterization and Synthesis of Hanford and SRS Tank Heel Materials

Abstract

The long-range objective of this study was to develop chemically assisted technologies for removing heels from tanks. In FY 01, the first two steps toward this objective were taken: (1) catalogue the occurrence and nature of tank heels and assess which materials are available for study and (2) develop methods for synthesizing non-radioactive surrogate heel materials for use in testing potential removal technologies. The chief finding of Task 1 was the existence of ''heels'', depending on the definition used. Hard materials that would be almost impossible to remove by sluicing are all but absent from the records of both Savannah River and Hanford. Historical usage suggests that the term ''heel'' may also apply to chunky, granular, or semi-solid pasty accumulations. These materials are documented and may also be difficult to remove by conventional sluicing technologies. Such heels may be comprised of normal sludge components, dominantly iron and aluminum hydroxides, or they may result from added materials which were not part of the normal fuel reprocessing operations: Portland cement, diatomaceous earth, sand and soil and spent zeolite ion exchange ''resins''. The occurrence and chemistry of the most notable ''heel'', that of the zeolite mass in Tank 19F at Savannah River, ismore » reviewed in some detail. Secondly, no clear correlation was found between high tank temperatures and difficulties encountered in removing materials from a tank at a later date; nor did the sludges from these tanks give any indication of being particularly solid. Experimental studies to develop synthetic heel materials were caned out using a number of different approaches. For normal sludge materials settling, even when assisted by a centrifuge, it proved ineffective. The same result was obtained from drying sludge samples. Even exposing sludges to a molten salt melt at 233 C, only produced a fine powder, rather than a resilient ceramic which resisted disaggregation. A cohesive material, however, was produced by wicking the pore fluid out of a sludge gel (into packed diatomaceous earth), while simultaneously applying pressure to compact the sludge as it dehydrated. Osmotic gradients could provide the same function as the capillary forces provided by the diatomaceous earth sorbant placed in contact with the sludge. Tests on the anomalous materials added to the tanks all indicated potential problems. Hard granules, and maybe chunks, may be encountered where Portland cement was added to a tank. Sand, spent zeolite resin, and diatomaceous earth, will all react with the tank fluids to produce a sodalite/cancrinite material. The degree of reaction determines whether the grains become cemented together. SRS activities showed that heels formed when spent zeolites were added to tanks can be readily dislodged and it is expected that heels from sand would possess equal or less cohesion. Diatomaceous earth may form more resilient crusts or masses. To summarize, the existence of ''hard'' heels has yet to be documented. A broader definition suggests inclusion of poorly cohesive cancrinite-cemented masses and dense past-like accumulations of abnormally compacted ''normal'' sludges. Chemical treatments to remove these materials must focus on agents that are active against aluminosilicates and hydrous oxides of iron and aluminum. Exploiting the high pore-water content of these materials may provide a second avenue for dislodging such accumulations. Techniques were developed to produce synthetic sludges on which various removal technologies could be tried.« less

Authors:
Publication Date:
Research Org.:
Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sandia National Lab. (SNL-CA), Livermore, CA (United States)
Sponsoring Org.:
US Department of Energy (US)
OSTI Identifier:
800783
Report Number(s):
SAND2002-0627
TRN: US0206078
DOE Contract Number:  
AC04-94AL85000
Resource Type:
Technical Report
Resource Relation:
Other Information: PBD: 1 Jul 2002
Country of Publication:
United States
Language:
English
Subject:
12 MANAGEMENT OF RADIOACTIVE WASTES, AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES; HANFORD RESERVATION; SAVANNAH RIVER PLANT; STORAGE FACILITIES; WASTE RETRIEVAL; RESIDUES; DIATOMACEOUS EARTH; ION EXCHANGE MATERIALS; PORTLAND CEMENT; SYNTHESIS; ZEOLITES

Citation Formats

KRUMHANSL, JAMES L. Occurrence, Characterization and Synthesis of Hanford and SRS Tank Heel Materials. United States: N. p., 2002. Web. doi:10.2172/800783.
KRUMHANSL, JAMES L. Occurrence, Characterization and Synthesis of Hanford and SRS Tank Heel Materials. United States. https://doi.org/10.2172/800783
KRUMHANSL, JAMES L. 2002. "Occurrence, Characterization and Synthesis of Hanford and SRS Tank Heel Materials". United States. https://doi.org/10.2172/800783. https://www.osti.gov/servlets/purl/800783.
@article{osti_800783,
title = {Occurrence, Characterization and Synthesis of Hanford and SRS Tank Heel Materials},
author = {KRUMHANSL, JAMES L},
abstractNote = {The long-range objective of this study was to develop chemically assisted technologies for removing heels from tanks. In FY 01, the first two steps toward this objective were taken: (1) catalogue the occurrence and nature of tank heels and assess which materials are available for study and (2) develop methods for synthesizing non-radioactive surrogate heel materials for use in testing potential removal technologies. The chief finding of Task 1 was the existence of ''heels'', depending on the definition used. Hard materials that would be almost impossible to remove by sluicing are all but absent from the records of both Savannah River and Hanford. Historical usage suggests that the term ''heel'' may also apply to chunky, granular, or semi-solid pasty accumulations. These materials are documented and may also be difficult to remove by conventional sluicing technologies. Such heels may be comprised of normal sludge components, dominantly iron and aluminum hydroxides, or they may result from added materials which were not part of the normal fuel reprocessing operations: Portland cement, diatomaceous earth, sand and soil and spent zeolite ion exchange ''resins''. The occurrence and chemistry of the most notable ''heel'', that of the zeolite mass in Tank 19F at Savannah River, is reviewed in some detail. Secondly, no clear correlation was found between high tank temperatures and difficulties encountered in removing materials from a tank at a later date; nor did the sludges from these tanks give any indication of being particularly solid. Experimental studies to develop synthetic heel materials were caned out using a number of different approaches. For normal sludge materials settling, even when assisted by a centrifuge, it proved ineffective. The same result was obtained from drying sludge samples. Even exposing sludges to a molten salt melt at 233 C, only produced a fine powder, rather than a resilient ceramic which resisted disaggregation. A cohesive material, however, was produced by wicking the pore fluid out of a sludge gel (into packed diatomaceous earth), while simultaneously applying pressure to compact the sludge as it dehydrated. Osmotic gradients could provide the same function as the capillary forces provided by the diatomaceous earth sorbant placed in contact with the sludge. Tests on the anomalous materials added to the tanks all indicated potential problems. Hard granules, and maybe chunks, may be encountered where Portland cement was added to a tank. Sand, spent zeolite resin, and diatomaceous earth, will all react with the tank fluids to produce a sodalite/cancrinite material. The degree of reaction determines whether the grains become cemented together. SRS activities showed that heels formed when spent zeolites were added to tanks can be readily dislodged and it is expected that heels from sand would possess equal or less cohesion. Diatomaceous earth may form more resilient crusts or masses. To summarize, the existence of ''hard'' heels has yet to be documented. A broader definition suggests inclusion of poorly cohesive cancrinite-cemented masses and dense past-like accumulations of abnormally compacted ''normal'' sludges. Chemical treatments to remove these materials must focus on agents that are active against aluminosilicates and hydrous oxides of iron and aluminum. Exploiting the high pore-water content of these materials may provide a second avenue for dislodging such accumulations. Techniques were developed to produce synthetic sludges on which various removal technologies could be tried.},
doi = {10.2172/800783},
url = {https://www.osti.gov/biblio/800783}, journal = {},
number = ,
volume = ,
place = {United States},
year = {Mon Jul 01 00:00:00 EDT 2002},
month = {Mon Jul 01 00:00:00 EDT 2002}
}