Irradiation performance of HTGR fuel rods in HFIR experiments HRB-7 and -8
The HRB-7 and -8 experiments were designed as a comprehensive test of mixed thorium-uranium oxide fissile particles with Th:U ratios from 0 to 8 for HTGR recycle application. In addition, fissile particles derived from Weak-Acid Resin (WAR) were tested as a potential backup type of fissile particle for HTGR recycle. These experiments were conducted at two temperatures (1250 and 1500/sup 0/C) to determine the influence of operating temperature on the performance parameters studied. The minor objectives were comparison of advanced coating designs where ZrC replaced SiC in the Triso design, testing of fuel coated in laboratory-scale equipment with fuel coated in production-scale coaters, comparison of the performance of /sup 233/U-bearing particles with that of /sup 235/U-bearing particles, comparison of the performance of Biso coatings with Triso coatings for particles containing the same type of kernel, and testing of multijunction tungsten-rhenium thermocouples. All objectives were accomplished. As a result of these experiments the mixed thorium-uranium oxide fissile kernel was replaced by a WAR-derived particle in the reference recycle design. A tentative decision to make this change had been reached before the HRB-7 and -8 capsules were examined, and the results of the examination confirmed the accuracy of the previous decision. Even maximum dilution (Th/U approximately equal to 8) of the mixed thorium-uranium oxide kernel was insufficient to prevent amoeba of the kernels at rates that are unacceptable in a large HTGR. Other results showed the performance of /sup 233/U-bearing particles to be identical to that of /sup 235/U-bearing particles, the performance of fuel coated in production-scale equipment to be at least as good as that of fuel coated in laboratory-scale coaters, the performance of ZrC coatings to be very promising, and Biso coatings to be inferior to Triso coatings relative to fission product retention.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- W-7405-ENG-26
- OSTI ID:
- 7290600
- Report Number(s):
- ORNL-5228; TRN: 77-011265
- Country of Publication:
- United States
- Language:
- English
Similar Records
Irradiation performance of HTGR fuel rods in HFIR experiment HRB-6
Interesting fuel for the HTGR
Related Subjects
COATED FUEL PARTICLES
PERFORMANCE TESTING
FUEL ELEMENTS
HTGR TYPE REACTORS
AMOEBA EFFECT
IRRADIATION
THORIUM OXIDES
URANIUM DIOXIDE
ACTINIDE COMPOUNDS
CHALCOGENIDES
FUEL PARTICLES
GAS COOLED REACTORS
GRAPHITE MODERATED REACTORS
OXIDES
OXYGEN COMPOUNDS
REACTOR COMPONENTS
REACTORS
TESTING
THORIUM COMPOUNDS
URANIUM COMPOUNDS
URANIUM OXIDES
210300* - Power Reactors
Nonbreeding
Graphite Moderated