Amorphization kinetics of Zr(Cr,Fe)[sub 2] under ion irradiation
- Pennsylvania State Univ., University Park, PA (United States). Dept. of Nuclear Engineering
- Atomic Energy of Canada Ltd., Chalk River, ON (Canada). Chalk River Labs.
- Argonne National Lab., IL (United States)
Thin foils of Zircaloy-4 were irradiated with 350 KeV [sup 40]Ar ions in the dual ion beam/HVEM facility at Argonne National Laboratory at 300--650 K. The irradiation-induced amorphization of the intermetallic precipitates Zr (Cr; Fe)[sub 2] and Zr[sub 2] (Ni, Fe) was studied in-situ. For Zr (Cr, Fe)[sub 2] precipitates the dose-to-amorphization was found to increase exponentially with temperature, with a critical temperature of about 650 K. The amorphization morphology was shown to be homogeneous, with no preferential site for nucleation, in contrast to neutron-irradiation amorphization which started at the precipitate-matrix interface. For Zr[sub 2] (Ni,Fe) precipitates it was found that amorphization occurred at 550 and 600 K, whereas in neutron irradiation no amorphization has been observed at those temperatures. The results are discussed in context of previous neutron and electron irradiations and likely amorphization mechanisms are proposed.
- Research Organization:
- Argonne National Lab., IL (United States)
- Sponsoring Organization:
- USDOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 6774091
- Report Number(s):
- ANL/MSD/CP-78354; CONF-921101-58; ON: DE93005560
- Resource Relation:
- Conference: 16. Material Research Society international symposium on the scientific basis for nuclear waste management fall meeting, Boston, MA (United States), 30 Nov - 5 Dec 1992
- Country of Publication:
- United States
- Language:
- English
Similar Records
A Simple Kinetic Model of Zircaloy Zr(Fe,Cr){sub 2} Precipitate Amorphization During Neutron Irradiation
In situ HVEM studies of phase transformation in Zr alloys and compounds under irradiation
Related Subjects
ZIRCALOY 4
PHYSICAL RADIATION EFFECTS
AMORPHOUS STATE
ARGON 40
ARGON IONS
CHROMIUM ALLOYS
INTERMETALLIC COMPOUNDS
ION BEAMS
IRON ALLOYS
KEV RANGE 100-1000
RADIATION DOSES
TEMPERATURE RANGE 0400-1000 K
ZIRCONIUM ALLOYS
ALLOY-ZR98SN-4
ALLOYS
ARGON ISOTOPES
BEAMS
CHARGED PARTICLES
CHROMIUM ADDITIONS
CORROSION RESISTANT ALLOYS
DOSES
ENERGY RANGE
EVEN-EVEN NUCLEI
HEAT RESISTANT MATERIALS
HEAT RESISTING ALLOYS
IONS
IRON ADDITIONS
ISOTOPES
KEV RANGE
LIGHT NUCLEI
MATERIALS
NUCLEI
RADIATION EFFECTS
STABLE ISOTOPES
TEMPERATURE RANGE
TIN ALLOYS
ZIRCALOY
ZIRCONIUM BASE ALLOYS
360106* - Metals & Alloys- Radiation Effects