On the Influence of Dispersoids on the Particle Stimulated Nucleation of Recrystallization in an Al-Fe-Si Model Alloy
The recrystallization of Al-alloys is controlled by precipitates. Whereas large particles generally promote recrystallization by particle stimulated nucleation, finely dispersed precipitates - either already present in the as-deformed state or precipitating during the recrystallization anneal - are known to strongly retard recrystallization. It was the aim of the present study to elucidate these concurring effects of large particles and small dispersoids on recrystallization in a ternary Al-Fe-Si model alloy. For that purpose, samples were prepared according to different pre-annealing treatments so as to comprise different states of precipitation and supersaturation. The evolution of microstructure and texture during rolling and recrystallization was characterized by metallography and by conventional X-ray texture analysis. EBSD-local texture investigations were employed to yield information on the efficiency of nucleation at the various nucleation sites and, consequently, on the influence of dispersoids on recrystallization.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Management and Administration, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 627132
- Report Number(s):
- LA-UR-97-4288; CONF-9709189-; ON: DE98003005; TRN: AD-a339 609
- Resource Relation:
- Conference: International conference on textures and anisotrohy of polycrystals, Claushal (Germany), 22-25 Sep 1997; Other Information: PBD: [Sep 1997]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of two-step homogenization on precipitation behavior of Al{sub 3}Zr dispersoids and recrystallization resistance in 7150 aluminum alloy
Texture development in Al-1. 8 wt% Cu depending on the precipitation state. 2: Recrystallization textures
Related Subjects
ALUMINIUM ALLOYS
NUCLEATION
IRON ALLOYS
PARTICLES
SILICON ALLOYS
RECRYSTALLIZATION
ANNEALING
MICROSTRUCTURE
BACKSCATTERING
X RADIATION
ELECTRONS
DIFFRACTION
SUPERSATURATION
TEXTURE
METALLOGRAPHY
DISPERSIONS
PRECIPITATION
TERNARY ALLOY SYSTEMS
DISPERSOIDS
ESBD(ELECTRON BACKSCATTERING DIFFRACTION)
PSN(PARTICLE STIMULATED NUCLEATION)