Recent results on the neutron irradiation of ITER candidate copper alloys irradiated in DR-3 at 250{degrees}C to 0.3 dpa
- Pacific Northwest National Lab., Richland, WA (United States)
Tensile specimens of CuCrZr and CuNiBe alloys were given various heat treatments corresponding to solution anneal, prime-ageing and bonding thermal treatment with additional specimens re-aged and given a reactor bakeout treatment at 350{degrees}C for 100 h. CuAl-25 was also heat treated to simulate the effects of a bonding thermal cycle on the material. A number of heat treated specimens were neutron irradiated at 250{degrees}C to a dose level of {approximately}0.3 dpa in the DR-3 reactor as Riso. The main effect of the bonding thermal cycle heat treatment was a slight decrease in strength of CuCrZr and CuNiBe alloys. The strength of CuAl-25, on the other hand, remained almost unaltered. The post irradiation tests at 250{degrees}C showed a severe loss of ductility in the case of the CuNiBe alloy. The irradiated CuAl-25 and CuCrZr specimens exhibited a reasonable amount of uniform elongation, with CuCrZr possessing a lower strength.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 543293
- Report Number(s):
- DOE/ER-0313/21; ON: DE97008798; TRN: 97:020335
- Resource Relation:
- Other Information: PBD: Apr 1997; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1996; PB: 296 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
The effect of bonding and bakeout thermal cycles on the properties of copper alloys irradiated at 100 C
Comparison of properties and microstructures of Trefimetaux and Hycon 3HP{trademark} after neutron irradiation