Fracture toughness of the IEA heat of F82H ferritic/martensitic stainless steel as a function of loading mode
- Pacific Northwest Labs., Richland, WA (United States)
- Washington State Univ., Pullman, WA (United States); and others
Mode I and mixed-mode I/III fracture toughness tests were performed for the IEA heat of the reduced activation ferritic/martensitic stainless steel F82H at ambient temperature in order to provide comparison with previous measurements on a small heat given a different heat treatment. The results showed that heat to heat variations and heat treatment had negligible consequences on Mode I fracture toughness, but behavior during mixed-mode testing showed unexpected instabilities.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 543286
- Report Number(s):
- DOE/ER-0313/21; ON: DE97008798; TRN: 97:020328
- Resource Relation:
- Other Information: PBD: Apr 1997; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1996; PB: 296 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Dependence of mode I and mixed mode I/III fracture toughness on temperature for a ferritic/martensitic stainless steel
Effect of loading modes and hydrogen on fracture toughness of a low activation ferritic/martensitic stainless steel
Effect of loading mode on the fracture toughness of a ferritic/martensitic stainless steel
Technical Report
·
Sat Apr 01 00:00:00 EST 1995
·
OSTI ID:543286
Effect of loading modes and hydrogen on fracture toughness of a low activation ferritic/martensitic stainless steel
Book
·
Sun Dec 31 00:00:00 EST 1995
·
OSTI ID:543286
+1 more
Effect of loading mode on the fracture toughness of a ferritic/martensitic stainless steel
Journal Article
·
Fri Sep 01 00:00:00 EDT 1995
· Metallurgical Transactions, A
·
OSTI ID:543286
+1 more