An evaluation of the susceptibility of V-4Cr-4Ti to stress corrosion cracking in room temperature DIII-D water
- Pacific Northwest National Lab., Richland, WA (United States)
Two fatigue precracked compact tension (CT) specimens of V-4Cr-4Ti were statically loaded to a stress intensity factor of about 30 MPa{radical}m in room temperature DIII-D water. The first specimen was tested for a period of about 30 days and the second specimen for about 54 days. At the conclusion of each test the specimens were fractured, and the fracture surfaces examined with a scanning electron microscope (SEM) to determine if SCC had occurred. No SCC was found in either test specimen.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- OSTI ID:
- 543269
- Report Number(s):
- DOE/ER-0313/21; ON: DE97008798; TRN: 97:020310
- Resource Relation:
- Other Information: PBD: Apr 1997; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1996; PB: 296 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mode I and mixed I/III crack initiation and propagation behavior of V-4Cr-4Ti alloy at 25{degrees}C
Effect of Oxygen on the Crack Growth Behavior of V-4Cr-4Ti at 600 degree C
Effect of Oxygen on the Crack Growth Behavior of V-4Cr-4Ti at 600C
Technical Report
·
Tue Apr 01 00:00:00 EST 1997
·
OSTI ID:543269
Effect of Oxygen on the Crack Growth Behavior of V-4Cr-4Ti at 600 degree C
Journal Article
·
Sun Dec 31 00:00:00 EST 2000
· Journal of Nuclear Materials, 283(Part B):822-826
·
OSTI ID:543269
Effect of Oxygen on the Crack Growth Behavior of V-4Cr-4Ti at 600C
Book
·
Fri Sep 01 00:00:00 EDT 2000
·
OSTI ID:543269