Electrical resistivity of V-Cr-Ti alloys
- Oak Ridge National Lab., TN (United States)
Room temperature electrical resistivity measurements have been performed on vanadium alloys containing 3-6%Cr and 3-6%Ti in order to evaluate the microstructural stability of these alloys. A nonlinear dependence on Cr and Ti concentration was observed, which suggests that either short range ordering or solute precipitation (perhaps in concert with interstitial solute clustering) has occurred in V-6Cr-6Ti.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- OSTI ID:
- 543267
- Report Number(s):
- DOE/ER-0313/21; ON: DE97008798; TRN: 97:020308
- Resource Relation:
- Other Information: PBD: Apr 1997; Related Information: Is Part Of Fusion materials semiannual progress report for the period ending December 31, 1996; PB: 296 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Cr and Ti contents on the recovery, recrystallization, and mechanical properties of vanadium alloys
Oxidation performance of V-Cr-Ti alloys
Feasibility of correlating V-Cr-Ti alloy weld strength with weld chemistry. CRADA final report
Technical Report
·
Mon Apr 01 00:00:00 EST 1996
·
OSTI ID:543267
+1 more
Oxidation performance of V-Cr-Ti alloys
Conference
·
Mon Apr 03 00:00:00 EDT 2000
·
OSTI ID:543267
Feasibility of correlating V-Cr-Ti alloy weld strength with weld chemistry. CRADA final report
Technical Report
·
Mon Jun 01 00:00:00 EDT 1998
·
OSTI ID:543267