Effects of partial oxidation of PMAN carbon on their performance as anodes in 1M LiPF{sub 6}/EC-DMC solutions
- Sandia National Labs., Albuquerque, NM (United States). Battery Development Dept.
A study was undertaken to examine the effects of partial oxidation on the electrochemical performance of carbons derived from poly(methylacrylonitrile) (PMAN)-divinylbenzene (DVB) co-polymers. Mild oxidation was examined as a possible technique to increase the reversible capacity, improve cycleability, and reduce the amount of irreversible capacity associated with the formation of the passivation layer during the first reduction. Oxidizing conditions involved treatment of the PMAN carbon prepared at 700 C with dry CO{sub 2} or with steam at 600 C for one hour. The effects on the performance in 1M LiPF{sub 6}/ethylene carbonate (EC)-dimethyl carbonate (DMC) solutions were evaluated by galvanostatic cycling tests, complex-impedance spectroscopy, and, to a more limited extent, cyclic voltammetry. Partial oxidation of PMAN carbon showed little or no overall beneficial effects in performance relative to the control.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 486069
- Report Number(s):
- SAND-96-2819C; CONF-970738-2; ON: DE97001240; TRN: AHC29713%%16
- Resource Relation:
- Conference: 2. international symposium on new materials for fuel cell and modern battery systems, Montreal (Canada), 6-10 Jul 1997; Other Information: PBD: [1996]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Temperature effects on the performance of PMAN-derived carbon anodes in 1M LiPF{sub 6}/EC-DMC solution
Effect on performance of composition of Li-ion carbon anodes derived from PMAN/DVB copolymers