IN-PILE LOOP CORROSION EXPERIMENTS WITH URANYL SULFATE SOLUTIONS AT 235 AND 250 C
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- DOE Contract Number:
- W-7405-ENG-26
- NSA Number:
- NSA-17-034348
- OSTI ID:
- 4667275
- Report Number(s):
- ORNL-3131
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-63
- Country of Publication:
- United States
- Language:
- English
Similar Records
INITIAL REPORT ON THE CORROSION OF FUSED TITANIA AND SYNTHETIC SAPPHIRES IN URANYL SULFATE SOLUTIONS AT 250 C
A MICROSCOPIC STUDY OF OXIDE FILMS FORMED ON CHROME-IRON CONTAINING APPROXIMATELY 1.25% COPPER EXPOSED TO 0.17 M URANYL SULFATE SOLUTION AT 250 C FOR 12 WEEKS
SUMMARY OF TOROID RUN NO. 84. TYPE 347 STAINLESS STEEL, TITANIUM 75A AND ZIRCALOY-2 IN URANYL SULFATE AT 250 C AND 25 fps. THE EFFECT IN LITHIUM SULFATE
Technical Report
·
Thu May 01 00:00:00 EDT 1952
·
OSTI ID:4667275
A MICROSCOPIC STUDY OF OXIDE FILMS FORMED ON CHROME-IRON CONTAINING APPROXIMATELY 1.25% COPPER EXPOSED TO 0.17 M URANYL SULFATE SOLUTION AT 250 C FOR 12 WEEKS
Technical Report
·
Wed Jan 23 00:00:00 EST 1952
·
OSTI ID:4667275
SUMMARY OF TOROID RUN NO. 84. TYPE 347 STAINLESS STEEL, TITANIUM 75A AND ZIRCALOY-2 IN URANYL SULFATE AT 250 C AND 25 fps. THE EFFECT IN LITHIUM SULFATE
Technical Report
·
Fri Feb 24 00:00:00 EST 1956
·
OSTI ID:4667275
Related Subjects
METALS, CERAMICS, AND OTHER MATERIALS
COPPER
CORROSION
DECOMPOSITION
DEUTERIUM COMPOUNDS
HEAVY WATER
HYDROGEN
IN PILE LOOPS
NICKEL
NICKEL SULFATES
OXYGEN
RADIATION CHEMISTRY
RADIATION DOSES
RADIOLYSIS
STAINLESS STEELS
SULFATES
SULFURIC ACID
TEMPERATURE
TENSILE PROPERTIES
TITANIUM ALLOYS
URANIUM OXIDES
URANIUM SULFATES
WATER
WEIGHT
ZIRCONIUM ALLOYS
COPPER
CORROSION
DECOMPOSITION
DEUTERIUM COMPOUNDS
HEAVY WATER
HYDROGEN
IN PILE LOOPS
NICKEL
NICKEL SULFATES
OXYGEN
RADIATION CHEMISTRY
RADIATION DOSES
RADIOLYSIS
STAINLESS STEELS
SULFATES
SULFURIC ACID
TEMPERATURE
TENSILE PROPERTIES
TITANIUM ALLOYS
URANIUM OXIDES
URANIUM SULFATES
WATER
WEIGHT
ZIRCONIUM ALLOYS