Ion beam modification of Tl-Ba-Ca-Cu-O type high temperature superconductors during irradiation
- Sandia National Labs., Albuquerque, NM (United States)
- New Mexico Univ., Albuquerque, NM (United States)
Microstructural modification of high temperature superconductor (HTS) single-crystal plates of Tl-1212 and Tl-2212 (numbers designate the Tl/Ba/Ca/Cu cation ratio) was studied during 1.5 MeV Kr{sup +} and Xe{sup +} ion irradiation with in-situ electron diffraction and after ion irradiation with high resolution TEM (HRTEM). Similar in-situ temperature dependence effects are seen for both phases. During irradiations from 22K to 673K, an amorphous halo develops after very low ion dose or fluence (1.7 {times} 10{sup 12} ions/cm{sup 2}). During irradiation at 100 and 300K, complete amorphization is obtained, while at 22 and {ge}533K, the halo fades slightly and a polycrystalline ring pattern develops, indicating ion irradiation induced crystallization occurred. After a low ion dose (8.5 {times} 10{sup 12} ions/cm{sup 2}) at 100 and 300K, HRTEM reveals amorphous regions 5-20 nm in size which are not columnar and do not all penetrate the entire sample thickness. At 22 and {ge}533K, Moire fringes and misoriented crystallites of cascade size are observed. The 4-6nm crystallites are thallium-rich.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 33139
- Report Number(s):
- SAND-94-1731C; CONF-941144-82; ON: DE95006807
- Resource Relation:
- Conference: Fall meeting of the Materials Research Society (MRS), Boston, MA (United States), 28 Nov - 9 Dec 1994; Other Information: PBD: [1994]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Near-Edge X-ray Absorption Fine-Structure Study of Ion-Beam-Induced Phase Transformation in Gd{sub 2}(Tl{sub 1-y}Zr{sub y}){sub 2}O{sub 7}
Effects of ion dose and irradiation temperature on the microstructure of three spinel compositions