Mechanical properties of high strength aluminum alloys formed by pulsed laser deposition
Very high-strength alloys of A1(O) have been formed using a pulsed laser deposition (PLD) system to deposit from alternating targets of A1 and A1{sub 2}O{sub 3}. Ion beam analysis and transmission electron microscopy show that the deposited material is uniform in composition with up to 33 at. % O and has a highly refined microstructure consisting of a fine, uniform dispersion of {approximately}1 nm diameter {gamma}-A1{sub 2}O{sub 3} precipitates. Ultra-low-load indentation testing combined with finite-element modeling is used to determine the mechanical properties of the layers. Yield stresses as high as 5.1 GPa have been measured in these materials, greatly exceeding the strengths of aerospace Al alloys (-0.5 GPa) and even high strength steels. The key to the properties of these materials is the dispersion of small, hard precipitates spaced only a few Burgers vectors apart; dislocations are apparently unable to cut through and must bow around them.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 164916
- Report Number(s):
- SAND-95-1406C; CONF-951153-17; ON: DE96003646
- Resource Relation:
- Conference: 9. international forum on electrolysis in the chemical industry: applied electrochemical technologies, Clearwater Beach, FL (United States), 5-9 Nov 1995; Other Information: PBD: [1995]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Exceptionally high-strength (@3 GPa) aluminum alloys demonstrated by oxygen ion implantation
Exceptionally high-strength ({approximately}3 GPa) aluminum alloys demonstrated by oxygen ion implantation