Effects of Oxide Film on the Corrosion Resistance of Titanium Grade 7 in Fluoride-Containing NaCl Brines
Conference
·
OSTI ID:15015905
The effects of oxide film on the corrosion behavior of Titanium Grade 7 (0.12-0.25% Pd) in fluoride-containing NaCl brines have been investigated. With the presence of a 0.6 {micro}m thick oxide layer, the annealed Ti grade 7 exhibited a significant improvement on the anodic polarization behavior. However, the oxide film did not demonstrate sustainable corrosion resistance in fluoride-containing solutions.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15015905
- Report Number(s):
- UCRL-CONF-208298; TRN: US200509%%516
- Resource Relation:
- Conference: Presented at: CORROSION 2005/NACE Conference, Houston, TX (US), 04/03/2005--04/07/2005; Other Information: PBD: 30 Nov 2004
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion Behavior of Titanium Grade 7 in Fluoride-Containing NaCl Brines
Corrosion Behavior of Titanium Grade 7 in Fluoride-Containing NaCl Brines
Anodic Polarization Behavior of Titanium Grade 7 in Dust Deliquescence Salt Environments
Conference
·
Tue May 18 00:00:00 EDT 2004
·
OSTI ID:15015905
Corrosion Behavior of Titanium Grade 7 in Fluoride-Containing NaCl Brines
Conference
·
Mon Oct 25 00:00:00 EDT 2004
·
OSTI ID:15015905
Anodic Polarization Behavior of Titanium Grade 7 in Dust Deliquescence Salt Environments
Conference
·
Fri Mar 09 00:00:00 EST 2007
·
OSTI ID:15015905