Key process parameters to modify the porosity of cerium dioxide microspheres formed in the internal gelation process
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Recently, an internal gelation study demonstrated that the use of heated urea and hexamethylenetetramine can have a pronounced impact on the porosity and sintering characteristics of cerium dioxide (CeO2) microspheres. This effort has identified process variables that can significantly change the initial porosity of the CeO2 microspheres with slight modifications. A relatively small difference in the sample preparation of cerium ammonium nitrate and ammonium hydroxide solution had a large reproducible impact on the porosity and slow pour density of the produced microspheres. Increases in the gelation temperature as small as 0.5 K also produced a noticeable increase in the slow pour density. If the gelation temperature was increased too high, the use of the heated hexamethylenetetramine and urea was no longer observed to be effective in increasing the porosity of the CeO2 microspheres. In conclusion, the final process variable was the amount of dispersing agent, Span™ 80, which can increase the slow pour density and produce significantly smaller microspheres.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1423099
- Alternate ID(s):
- OSTI ID: 1549842
- Journal Information:
- Journal of Nuclear Materials, Vol. 495, Issue C; ISSN 0022-3115
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Similar Records
Production of cerium dioxide microspheres by an internal gelation sol–gel method
Key properties of mixed cerium and zirconium microspheres prepared by the internal gelation process with previously boiled HMTA and urea