Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement
- Brookhaven National Lab. (BNL), Upton, NY (United States)
This study evaluates inorganic pigments for improving carbon steel (CS) brine-corrosion protection by the sodium metasilicate-activated calcium aluminate cement/Fly Ash blend at 300°C. Calcium borosilicate (CBS) and zinc phosphate, significantly improved CS corrosion-protection by decreasing cement’s permeability for corrosive ions and inhibiting anodic corrosion. An amorphous Na2O-Al2O3-SiO2-H2O phase tightly attached to CS surface formed at 300oC in CBS-modified cement pore solution. The corrosion rate of the CS covered with this phase was nearly 4-fold lower than in the case of nonmodified cement pore solution where the major phase formed on the surface of CS was crystalline analcime.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- SC00112704
- OSTI ID:
- 1183248
- Report Number(s):
- BNL-107118-2014-IR; R&D Project: 20437
- Country of Publication:
- United States
- Language:
- English
Similar Records
Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement
Self-healing, re-adhering, and carbon-steel corrosion mitigating properties of fly ash-containing calcium aluminum phosphate cement composite at 300 °C hydrothermal temperature
Hot alkali carbonation of sodium metaphosphate modified fly ash/calcium aluminate blend hydrothermal cements
Technical Report
·
Sat Nov 01 00:00:00 EDT 2014
·
OSTI ID:1183248
Self-healing, re-adhering, and carbon-steel corrosion mitigating properties of fly ash-containing calcium aluminum phosphate cement composite at 300 °C hydrothermal temperature
Journal Article
·
Sat Feb 16 00:00:00 EST 2019
· Cement and Concrete Composites
·
OSTI ID:1183248
Hot alkali carbonation of sodium metaphosphate modified fly ash/calcium aluminate blend hydrothermal cements
Journal Article
·
Fri Nov 01 00:00:00 EST 1996
· Cement and Concrete Research
·
OSTI ID:1183248