Polyethylene encapsulation of simulated blowdown waste for SEG treatability study. Letter report on Phase I screening: Waste treatment and specimen preparation
The Environmental and Waste Technology Center is a participating subcontractor in the Scientific Ecology Group (SEG) Treatability Study for Westinghouse Savannah River Co.`s Blowdown Waste. This waste will be generated at the Consolidated Incinerator Facility (CIF) and will consist of the neutralized aqueous scrubber solution from the incinerator. Since the facility is designed to burn low-level radioactive, hazardous, and mixed wastes, the blowdown waste will likely be a mixed waste. Polyethylene encapsulation is an improved treatment method that has been developed at BNL over the last 10 years. Polyethylene is an inert, thermoplastic polymer with a melt temperature of 120 C. The BNL process is a modification of standard plastics extrusion technology that has been utilized successfully by the plastics industry for over 50 years. Polyethylene binder and dry waste material are fed through separate calibrated feeders to the extruder, where the materials are thoroughly mixed, heated to a molten condition, and then extruded into a suitable mold. A monolithic solid waste form results on cooling. The objective of the Phase 1 screening effort was to prepare test specimens of CIF surrogate waste encapsulated in polyethylene for leach testing using EPA`s Toxicity Characteristic Leaching Procedure (TCLP). BNL received aqueous CIF surrogate from SEG, pretreated the stimulant for processing, and fabricated TCLP test specimens for analysis at an independent laboratory. Laboratory and processing procedures are described in this letter report.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC02-76CH00016
- OSTI ID:
- 10132667
- Report Number(s):
- BNL-49738; ON: DE94008092; TRN: 94:005688
- Resource Relation:
- Other Information: PBD: 17 Aug 1993
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stabilization of high salt wastes by polymer extrusion
Polyethylene encapsulation of molten salt oxidation mixed low-level radioactive salt residues
Related Subjects
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS
SAVANNAH RIVER PLANT
INCINERATORS
SOLID WASTES
ENCAPSULATION
WASTE FORMS
LEACHING
RADIOACTIVE WASTE PROCESSING
ENVIRONMENTAL IMPACTS
PERFORMANCE TESTING
SILVER
ARSENIC
BARIUM
CADMIUM
CHROMIUM
MERCURY
NICKEL
LEAD
ANTIMONY
SELENIUM
THALLIUM
ZINC
052001
053000
WASTE PROCESSING
ENVIRONMENTAL ASPECTS