Fabrication and testing of Rutherford-type cables for react and wind accelerator magnets
A common coil design for a high-field accelerator dipole magnet using a Nb{sub 3}Sn cable with the React-and-Wind approach is pursued by a collaboration between Fermilab and LBNL. The design requirements for the cable include a high operating current so that a field of 10-11 T can be produced, together with a low critical current degradation due to bending around a 90 mm radius. A program, using ITER strands of the internal tin type, was launched to develop the optimal cable design for React-and-Wind common coil magnets. Three prototype cable designs, all 15 mill wide, were fabricated: a 41-strand cable with 0.7 mm diameter strands; a 57-strand cable with 0.5 mm diameter strands; and a 259 strand multi-level cable with a 6-around-1 sub-element using 0.3 mm diameter wire. Two versions of these cables were fabricated: one with no core and one with a stainless steel core. Additionally, the possibility of a wide (22 mm) cable made from 0.7 mm strand was explored. This paper describes the first results of the cable program including reports on cable fabrication and reaction, first winding tests and first results of the measurement of the critical current degradation due to cabling and bending.
- Research Organization:
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- Accelerator& Fusion Research Division
- DOE Contract Number:
- DE-AC02-05CH11231
- OSTI ID:
- 1011736
- Report Number(s):
- LBNL-45189; TRN: US201109%%574
- Resource Relation:
- Conference: Applied Superconductivity Conference 2000, Virginia Beach, VA, September 17 - 22, 2000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Design Modifications, Fabrication and Test of HFDB-03 Racetrack Magnet Wound with Pre-Reacted Nb3Sn Rutherford Cable
Study of the react and wind technique for a Nb(3)Sn common coil dipole