Effect of Filler Concentration on Thermal Stability of Vinyl Copolymer Elastomer (VCE) Composites
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
To study the thermal stability of vinyl copolymer elastomer (VCE) in its composite form, systematic TGA characterizations were conducted in both nonisothermal and isothermal modes. The effects of filler concentration on the aging behaviors of the VCE/filler composites were investigated under nitroplasticizer (NP) environment. FTIR characterization was used to probe the structural changes in the VCE polymer before and after the thermal treatments. This study suggests that the filler concentration significantly deteriorates the thermal stability of NP at a moderate temperature (< 70 °C). The degradation of NP, in turn, accelerates the aging process of the VCE polymer in its composite form.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1172203
- Report Number(s):
- LA-UR-15-21679
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermal stability of filler‐based ethylene/vinyl acetate/vinyl alcohol terpolymer in nitroplasticizer oxidative environment
Aging Studies of VCE Dismantlement Returns
Boron-filled elastomers (SANL 252-056). [Vinyl copolymer; Viton A fluoroelastomer; physical characteristics]
Journal Article
·
Sat Dec 25 00:00:00 EST 2021
· Journal of Vinyl & Additive Technology
·
OSTI ID:1172203
+2 more
Aging Studies of VCE Dismantlement Returns
Technical Report
·
Mon Oct 17 00:00:00 EDT 2011
·
OSTI ID:1172203
+5 more
Boron-filled elastomers (SANL 252-056). [Vinyl copolymer; Viton A fluoroelastomer; physical characteristics]
Technical Report
·
Tue Apr 20 00:00:00 EST 1976
·
OSTI ID:1172203