Experimental measurement of the principal isentrope for aluminum 6061-T6 to 240 GPa.
Journal Article
·
· Proposed for publication in Physical Review Letters.
OSTI ID:990431
Using a magnetic pressure drive, an absolute measurement of stress and density along the principal compression isentrope is obtained for solid aluminum to 240 GPa. Reduction of the free-surface velocity data relies on a backward integration technique, with approximate accounting for unknown systematic errors in experimental timing. Maximum experimental uncertainties are {+-}4.7% in stress and {+-}1.4% in density, small enough to distinguish between different equation-of-state (EOS) models. The result agrees well with a tabular EOS that uses an empirical universal zero-temperature isotherm.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 990431
- Report Number(s):
- SAND2005-0729J; TRN: US201020%%375
- Journal Information:
- Proposed for publication in Physical Review Letters., Journal Name: Proposed for publication in Physical Review Letters.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Experimental measurement of the principal isentrope for aluminum 6061-T6 to 240 GPa.
Effect of material strength on the relationship between the principal Hugoniot and quasi-isentrope of beryllium and 6061-T6 aluminum below 35 GPa
Isotherms Reduced from Isentropes and Hugoniots up to Several 100 GPa
Journal Article
·
Wed Feb 01 00:00:00 EST 2006
· Proposed for publication in the Journal of Applied Physics.
·
OSTI ID:990431
Effect of material strength on the relationship between the principal Hugoniot and quasi-isentrope of beryllium and 6061-T6 aluminum below 35 GPa
Journal Article
·
Fri Mar 01 00:00:00 EST 1985
· J. Appl. Phys.; (United States)
·
OSTI ID:990431
Isotherms Reduced from Isentropes and Hugoniots up to Several 100 GPa
Journal Article
·
Fri Jul 28 00:00:00 EDT 2006
· AIP Conference Proceedings
·
OSTI ID:990431