A Feasiblity Study on Spot Friction Welding of Magnesium Alloy AZ31
- ORNL
- Ford Motor Company
Spot friction welding (SFW) is a novel variant of the linear friction stir welding process with the potential to create strong joints between similar, as well as dissimilar sheet metals. It is particularly suitable for soft, low melting point metals such as aluminum, magnesium, and their alloys where resistance spot welding can cause defects such as voids, trapped gas and micro-cracks due to the intense heat requirement for joint formation. Up to now, spot friction welding has focused primarily on aluminum alloys. This paper presents a feasibility study on spot friction welding of AZ31, a wrought magnesium alloy available in sheet form. Lap joints of 1.58-mm-thick magnesium alloy AZ31B-O sheet were produced by spot friction welding. The spot welds were made in 2 sec with 15-mm-diameter pin tool rotating at 500-2,000 rpm. The tool was inserted into 2-sheet stack-ups to depths of either 2.4 or 2.8 mm relative to the top sheet surface. Tensile-shear testing showed that joint strengths up to 4.75 kN were obtained. The removal of surface oxides from the sheets prior to welding increased lap shear strengths about 50% at the 2.4-mm insertion depth and it promoted failure by nugget pull-out rather than by interface separation.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 981750
- Resource Relation:
- Conference: 63rd Annual World Magnesium Conference, Beijing, China, 20060521, 20060524
- Country of Publication:
- United States
- Language:
- English
Similar Records
Friction stir welding joint of dissimilar materials between AZ31B magnesium and 6061 aluminum alloys: Microstructure studies and mechanical characterizations
Mechanical and microstructural characterization of AZ31 magnesium‑carbon fiber reinforced polymer joint obtained by friction stir interlocking technique