Cracking resistance in steam pipe fittings having various microdamage levels
Journal Article
·
· Strength of Materials
OSTI ID:96649
Cracking resistance and metal damage are considered in relation to structural state for steam-pipe fittings during use. An approximate scheme is given for estimating the maximum permissible operating time in the plastic state in relation to the depth of an observed crack-type defect.
- OSTI ID:
- 96649
- Journal Information:
- Strength of Materials, Vol. 26, Issue 9; Other Information: PBD: May 1995; TN: Translated from Problemy Prochnosti; No. 9, 48-52(Sep 1994)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Validation of creep crack growth life estimation methodology/hot reheat steam pipes
Experimental and analytical assessment of circumferential through-wall cracked pipes under pure bending
Change in the crack resistance of steam pipes of steel 12Kh1MF as a result of long service
Journal Article
·
Mon Aug 01 00:00:00 EDT 1994
· Journal of Pressure Vessel Technology; (United States)
·
OSTI ID:96649
Experimental and analytical assessment of circumferential through-wall cracked pipes under pure bending
Technical Report
·
Mon Sep 01 00:00:00 EDT 1986
·
OSTI ID:96649
Change in the crack resistance of steam pipes of steel 12Kh1MF as a result of long service
Journal Article
·
Thu May 01 00:00:00 EDT 1986
· Sov. Mater. Sci. (Engl. Transl.); (United States)
·
OSTI ID:96649
+1 more