Investigation of CdZnS Buffer Layers on the Performance of CuInGaSe2 and CuGaSe2 Solar Cells
Cu(In,Ga)Se{sub 2} (CIGS) and CuGaSe{sub 2} (CGS) solar cells were fabricated using Cd{sub 1-x}Zn{sub x}S (CdZnS) buffer layers prepared by chemical bath deposition (CBD) with relative Zn compositions in the CBD bath values of X{sub bath} = 0 (i.e., pure CdS), 0.1, 0.2, 0.3, 0.4, and 0.5. The cell performance parameters of CIGS and CGS films treated with a KCN solution were investigated and compared to cells without KCN treatment. It was found that absorber films treated with KCN etching prior to the buffer CBD step show an improved cell performance for both the CIGS and CGS cells deposited with either CdS or CdZnS buffer layer. A CIGS cell with CdZnS buffer layer of X{sub bath} = 0.2 produced a 13% AM1.5G conversion efficiency with higher V{sub oc}, J{sub sc}, and FF values as compared to the CdZnS/CIGS cells with different Zn contents. Results of photo- J-V and quantum efficiency (QE) measurements reveal that the CGS cell with CdZnS buffer layer of X{sub bath} = 0.3 performed better than the CGS cell deposited with a pure CdS buffer layer. This result is suggested as a result of an increased photocurrent at shorter wavelengths and a more favorable conduction band-offset at the CdZnS/CGS junction.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC36-99-GO10337
- OSTI ID:
- 943985
- Resource Relation:
- Conference: [Proceedings] 2006 IEEE 4th World Conference on Photovoltaic Energy Conversion (WCPEC-4), 7-12 May 2006, Waikoloa, Hawaii
- Country of Publication:
- United States
- Language:
- English
Similar Records
Optical properties of Cd{sub 1-x}Zn{sub x}S thin films for CuInGaSe{sub 2} solar cell application
Research on Polycrystalline Thin-Film CuInGaSe2 Solar Cells: Annual Subcontract Report, 3 May 1991 - 21 May 1993