Title: High strength ferritic alloy-D53

A high strength ferritic alloy is described having from about 0.2% to about 0.8% by weight nickel, from about 2.5% to about 3.6% by weight chromium, from about 2.5% to about 3.5% by weight molybdenum, from about 0.1% to about 0.5% by weight vanadium, from about 0.1% to about 0.5% by weight silicon, from about 0.1% to about 0.6% by weight manganese, from about 0.12% to about 0.20% by weight carbon, from about 0.02% to about 0.1% by weight boron, a maximum of about 0.05% by weight nitrogen, a maximum of about 0.02% by weight phosphorous, a maximum of about 0.02% by weight sulfur, and the balance iron.
Authors:
 [1] ;  [2] ;  [3]
  1. (Ann Arbor, MI)
  2. (Springfield, VA)
  3. (Richland, WA)
Publication Date:
OSTI Identifier:
862925
Report Number(s):
US 4049432
DOE Contract Number:
E(45-1)-2170
Resource Type:
Patent
Research Org:
Pacific Northwest National Laboratory (PNNL), Richland, WA (United States)
Country of Publication:
United States
Language:
English
Subject:
strength; ferritic; alloy-d53; strength; ferritic; alloy; described; weight; nickel; weight; chromium; weight; molybdenum; weight; vanadium; weight; silicon; weight; manganese; 12; 20; weight; carbon; 02; weight; boron; maximum; 05; weight; nitrogen; maximum; 02; weight; phosphorous; maximum; 02; weight; sulfur; balance; iron; weight sulfur; balance iron; strength ferritic; strength ferritic; ferritic alloy; ferritic alloy; weight phosphorous; weight carbon; weight molybdenum; weight chromium; weight boron /420/148/