Aging characteristics of electron beam and gas tungsten arc fusion zones of Al-Cu-Li alloy 2090
- Lawrence Berkeley Lab., CA (United States). Center for Advanced Materials
- Univ. of California, Berkeley, CA (United States). Dept of Materials Science and Engineering
A transmission electron microscopy (TEM) investigation of the electron beam (EB) and gas tungsten arc (GTA) fusion zones of 2090 indicates that in both the as-welded and aged conditions, the EB and GTA fusion zones lack the volume fraction and the homogeneity of strengthening precipitates found in the base metal. In the underaged and peak-aged conditions, the [delta][prime] phase is the primary strengthener, the volume fraction of T[sub 1] present being too low to be effective. The T[sub 1] precipitates are found either in the vicinity of other inclusions or at the dendrite boundaries. As the strength increases with postweld aging, the elongation decreased to 1%. The presence of the boundary phases and Cu- and Cl-containing inclusions at the boundaries leads to poor elongation. The joint efficiencies of the peak-aged EB and GTA weldments (EBWs and GTAWs, respectively) are 75 and 55% at 293 K and 75 and 50% at 77 K, respectively. Both EBWs and GTAWs have relatively low elongations.
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 7244375
- Journal Information:
- Metallurgical Transactions, A (Physical Metallurgy and Materials Science); (United States), Vol. 22; ISSN 0360-2133
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of precipitate distribution on 293 K and 77 K properties of 2090-T81 weldments
Microstructure and properties of AA 2090 weldments
Related Subjects
ALUMINIUM BASE ALLOYS
ELECTRON BEAM WELDING
GAS TUNGSTEN-ARC WELDING
COPPER ALLOYS
LITHIUM ALLOYS
WELDED JOINTS
MECHANICAL PROPERTIES
MICROSTRUCTURE
AGING
EXPERIMENTAL DATA
HEAT AFFECTED ZONE
PRECIPITATION
PRECIPITATION HARDENING
ALLOYS
ALUMINIUM ALLOYS
ARC WELDING
DATA
FABRICATION
GAS METAL-ARC WELDING
HARDENING
INFORMATION
JOINING
JOINTS
NUMERICAL DATA
SEPARATION PROCESSES
WELDING
ZONES
360102* - Metals & Alloys- Structure & Phase Studies
360103 - Metals & Alloys- Mechanical Properties