Microwave absorption studies of high T sub c superconductors and related materials 8; ESR of DPPH coated on BiSrCaCuO films fabricated on MgO (100) substrates
- Superconductivity Research Lab., ISTEC, 10-13, Shinonome 1-chome, Koto-ku, Tokyo 135 (JP)
This paper reports that ESR of DPPH coated on Bi-Sr-Ca-Cu-O films fabricated on MgO (100) substrates by MOCVD have been studied for samples with different thicknesses, 1000 {Angstrom} and 100 {Angstrom}. Temperature dependence of the ESR peak-to-peak linewidth, {Delta}H{sub pp}, revealed that {Delta}H{sub pp} increases with film thickness. The Excess ESR linewidth, {delta}({Delta}H{sub pp}) was also analyzed in terms of (1 {minus} t{sup alpha}, with t = T/T{sub c}, giving for example {alpha} = 4 ={minus}1 for the 1000 {Angstrom} thick sample. The ESR lineshapes were distorted by rotating the samples in applied magnetic fields. Severe distortion was found for the 1000 {Angstrom} sample below about 30 K, but the distortion almost disappears at temperatures above 30 K. The applied magnetic field effects were also examined in both field-cooled and zero-field-cooled cases.
- OSTI ID:
- 7088646
- Journal Information:
- Modern Physics Letters B; (Singapore), Vol. 6:14; ISSN 0217-9849
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microwave absorption studies on high-T sub c superconductors and related materials II; Electron spin resonance of DPPH coated on Y sub 1 Ba sub 2 Cu sub 3 O sub y as a probe of magnetic field variations
Microwave absorption studies on high-T sub c superconductors and related materials IV ESR as a probe of flux pinning in Y-Ba-Cu-O superconductors prepared by the MPMG method
Related Subjects
71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
BISMUTH COMPOUNDS
COATINGS
CALCIUM COMPOUNDS
STRONTIUM COMPOUNDS
ABSORPTION SPECTRA
CHEMICAL VAPOR DEPOSITION
CUPRATES
DPPH
ELECTRON SPIN RESONANCE
HIGH-TC SUPERCONDUCTORS
MAGNESIUM OXIDES
MICROWAVE SPECTRA
ORGANIC COMPOUNDS
SUPERCONDUCTING FILMS
TEMPERATURE DEPENDENCE
THICKNESS
ALKALINE EARTH METAL COMPOUNDS
CHALCOGENIDES
CHEMICAL COATING
COPPER COMPOUNDS
DEPOSITION
DIMENSIONS
FILMS
MAGNESIUM COMPOUNDS
MAGNETIC RESONANCE
NITRO COMPOUNDS
ORGANIC NITROGEN COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
RADICALS
RESONANCE
SPECTRA
SUPERCONDUCTORS
SURFACE COATING
TRANSITION ELEMENT COMPOUNDS
360207* - Ceramics
Cermets
& Refractories- Superconducting Properties- (1992-)
661200 - Techniques of General Use in Physics- (1992-)