Current understanding of stress-corrosion cracking
Journal Article
·
· JOM (Journal of the Minerals, Metals and Materials Society); (United States)
- Newcastle upon Tyne Univ. (United Kingdom)
The mechanisms that cause stress corrosion cracking and the conditions in which they apply are reviewed. Attention is given to hydrogen-assisted cracking, film-induced cleavage, dissolution mechanisms, surface-mobility mechanism, cracking environments, deformation and cracking, and stochastic aspects of cracking. 70 refs.
- OSTI ID:
- 6208889
- Journal Information:
- JOM (Journal of the Minerals, Metals and Materials Society); (United States), Vol. 44:12; ISSN 1047-4838
- Country of Publication:
- United States
- Language:
- English
Similar Records
Irradiation-assisted stress corrosion cracking considerations at temperatures below 288{degree}C
Hydrogen embrittlement and stress corrosion cracking
Insights into Stress Corrosion Cracking Mechanisms from High-Resolution Measurements of Crack-Tip Structures and Compositions
Technical Report
·
Wed Mar 01 00:00:00 EST 1995
·
OSTI ID:6208889
Hydrogen embrittlement and stress corrosion cracking
Book
·
Sun Jan 01 00:00:00 EST 1984
·
OSTI ID:6208889
Insights into Stress Corrosion Cracking Mechanisms from High-Resolution Measurements of Crack-Tip Structures and Compositions
Conference
·
Thu Nov 25 00:00:00 EST 2004
·
OSTI ID:6208889
Related Subjects
36 MATERIALS SCIENCE
CHROMIUM ALLOYS
CRACK PROPAGATION
CRACKS
STRESS CORROSION
NICKEL ALLOYS
FATIGUE
GRAIN BOUNDARIES
HYDROGEN EMBRITTLEMENT
INTERGRANULAR CORROSION
PLASTICITY
ALLOYS
CHEMICAL REACTIONS
CORROSION
EMBRITTLEMENT
MECHANICAL PROPERTIES
MICROSTRUCTURE
360103* - Metals & Alloys- Mechanical Properties
CHROMIUM ALLOYS
CRACK PROPAGATION
CRACKS
STRESS CORROSION
NICKEL ALLOYS
FATIGUE
GRAIN BOUNDARIES
HYDROGEN EMBRITTLEMENT
INTERGRANULAR CORROSION
PLASTICITY
ALLOYS
CHEMICAL REACTIONS
CORROSION
EMBRITTLEMENT
MECHANICAL PROPERTIES
MICROSTRUCTURE
360103* - Metals & Alloys- Mechanical Properties