Mechanical properties of laser welded aluminum alloys
- Univ. of Illinois, Urbana-Champaign, IL (United States)
- Univ. of Michigan, Ann Arbor, MI (United States)
The demand for lighter weight vehicles has prompted accelerated development in processing aluminum alloys for automobile structural applications. One of the current research initiatives centers on laser beam welding of aluminum alloys. Autogenous butt welds have been performed on Al 3003, 5754, 6111, and 6061-T6 plates with a 6 kW CO2 laser. For 6061, tensile data indicate about 60% of the base metal strength was attained in the as-welded condition, with a brittle fracture occurring through the weld. A post-weld heat treatment to the T6 condition resulted in a recovery of original ultimate tensile strengths, although these also failed in the weld. Hardness measurements of the post-weld T6 reveal a uniform hardness across the HAZ and fusion zone that is comparable to the original hardness. All 3003 welds fractured in the parent material in a ductile fashion. A high quality bead was consistently achieved with the 3003 alloy, whereas the other alloys demonstrated bead irregularities. SEM photographs reveal large, spherical pores, suggesting that they were formed by gas entrapment rather than by shrinkage.
- OSTI ID:
- 535592
- Report Number(s):
- CONF-961073-; TRN: 97:003388-0002
- Resource Relation:
- Conference: ICALEO `96: 15. international congress on applications of lasers and electro-optics, Detroit, MI (United States), 14-17 Oct 1996; Other Information: PBD: 1996; Related Information: Is Part Of Proceedings of the lasers and electro-optics for automotive manufacturing conference - ICALEO `96. Volume 82; PB: 181 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Laser beam welding of aluminum alloy 5754-O using a 3 kW Nd:YAG laser and fiber optic beam delivery
Ultrafine grained structure and improved mechanical properties of low temperature friction stir spot welded 6061-T6 Al alloys