Irradiation effects on interlaminar shear strength of GFRP at low temperature
Journal Article
·
· Advances in Cryogenic Engineering
OSTI ID:476700
- Osaka Univ. (Japan); and others
The degradation of interlaminar shear strength (ILSS) of GFRPs has been evaluated after 77K electron and 20K reactor irradiation. The GFRPs used in this work were prepared using several matrix resins. Optical microscopic observations of the fracture surfaces were carried out to determine the degradation behavior of ILSS. The fiber exposed area of fracture (interfacial failure) surface was found to be larger with higher absorbed dose. It suggested that the degradation of ILSS was induced by the interface failure between fiber and matrix. The matrix resin was also found to be degraded along with the interface.
- OSTI ID:
- 476700
- Report Number(s):
- CONF-950722-; ISSN 0065-2482; TRN: 97:009191
- Journal Information:
- Advances in Cryogenic Engineering, Vol. 42A; Conference: CEC/ICMC `95: cryogenic engineering conference and international cryogenic materials conference, Columbus, OH (United States), 17-21 Jul 1995; Other Information: PBD: 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
FISSION NEUTRON IRRADIATION EFFECT ON INTERLAMINAR SHEAR STRENGTH OF CYANATE ESTER RESIN GFRP AT RT AND 77 K
EFFECT OF GAMMA RAY IRRADIATION ON INTERLAMINAR SHEAR STRENGTH OF GLASS FIBER REINFORCED PLASTICS AT 77 K
Electron radiation effects on Mode II interlaminar fracture toughness of GFRP and CFRP composites
Journal Article
·
Thu Apr 08 00:00:00 EDT 2010
· AIP Conference Proceedings
·
OSTI ID:476700
+4 more
EFFECT OF GAMMA RAY IRRADIATION ON INTERLAMINAR SHEAR STRENGTH OF GLASS FIBER REINFORCED PLASTICS AT 77 K
Journal Article
·
Mon Mar 03 00:00:00 EST 2008
· AIP Conference Proceedings
·
OSTI ID:476700
Electron radiation effects on Mode II interlaminar fracture toughness of GFRP and CFRP composites
Journal Article
·
Sun Jan 01 00:00:00 EST 1989
· SAMPE Q.; (United States)
·
OSTI ID:476700