Shear compression testing of glass-fibre steel specimens after 4K reactor irradiation: Present status and facility upgrade
- Fakultaet fuer Physik, Garching (Germany)
- The NET-Team, Garching (Germany); and others
The shear strengths of various fibre reinforced resins being promising candidate insulators for superconducting coils to be used tinder a strong radiation load, e.g. in future fusion reactors were investigated prior and subsequent to reactor in-core irradiation at liquid helium temperature. A large number of sandwich-like (steel-bonded insulation-steel) specimens representing a widespread variety of materials and preparation techniques was exposed to irradiation doses of up to 5 x 10{sup 7} Gy in form of fast neutrons and {gamma}-radiation. In a systematic study several experimental parameters including irradiation dose, postirradiation storage temperature and measuring temperature were varied before the determination of the ultimate shear strength. The results obtained from the different tested materials are compared. In addition an upgrade of the in-situ test rig installed at the Munich research reactor is presented, which allows combined shear/compression loading of low temperature irradiated specimens and provides a doubling of the testing rate.
- OSTI ID:
- 476685
- Report Number(s):
- CONF-950722-; ISSN 0065-2482; TRN: 97:009176
- Journal Information:
- Advances in Cryogenic Engineering, Vol. 42A; Conference: CEC/ICMC `95: cryogenic engineering conference and international cryogenic materials conference, Columbus, OH (United States), 17-21 Jul 1995; Other Information: PBD: 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Insulation interlaminar shear strength testing with compression and irradiation
Shear strength of irradiated insulation under combined shear/compression loading