High-precision measurements of the compressibility of chalcogenide glasses at a hydrostatic pressure up to 9 GPa
- Universite du Littoral, LPCA, UMR 8101 CNRS (France)
- Vereshchagin Institute of High-Pressure Physics (Russian Federation)
The volumes of glassy germanium chalcogenides GeSe{sub 2}, GeS{sub 2}, Ge{sub 17}Se{sub 83}, and Ge{sub 8}Se{sub 92} are precisely measured at a hydrostatic pressure up to 8.5 GPa. The stoichiometric GeSe{sub 2} and GeS{sub 2} glasses exhibit elastic behavior in the pressure range up to 3 GPa, and their bulk modulus decreases at pressures higher than 2–2.5 GPa. At higher pressures, inelastic relaxation processes begin and their intensity is proportional to the logarithm of time. The relaxation rate for the GeSe{sub 2} glasses has a pronounced maximum at 3.5–4.5 GPa, which indicates the existence of several parallel structural transformation mechanisms. The nonstoichiometric glasses exhibit a diffuse transformation and inelastic behavior at pressures above 1–2 GPa. The maximum relaxation rate in these glasses is significantly lower than that in the stoichiometric GeSe{sub 2} glasses. All glasses are characterized by the “loss of memory” of history: after relaxation at a fixed pressure, the further increase in the pressure returns the volume to the compression curve obtained without a stop for relaxation. After pressure release, the residual densification in the stoichiometric glasses is about 7% and that in the Ge{sub 17}Se{sub 83} glasses is 1.5%. The volume of the Ge{sub 8}Se{sub 92} glass returns to its initial value within the limits of experimental error. As the pressure decreases, the effective bulk moduli of the Ge{sub 17}Se{sub 83} and Ge{sub 8}Se{sub 92} glasses coincide with the moduli after isobaric relaxation at the stage of increasing pressure, and the bulk modulus of the stoichiometric GeSe{sub 2} glass upon decreasing pressure noticeably exceeds the bulk modulus after isobaric relaxation at the stage of increasing pressure. Along with the reported data, our results can be used to draw conclusions regarding the diffuse transformations in glassy germanium chalcogenides during compression.
- OSTI ID:
- 22617205
- Journal Information:
- Journal of Experimental and Theoretical Physics, Vol. 123, Issue 2; Other Information: Copyright (c) 2016 Pleiades Publishing, Inc.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1063-7761
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure of germanium-selenium glasses: An x-ray-absorption fine-structure study
Bulk Glassy GeTe2: A Missing Member of the Tetrahedral GeX2 Family and a Precursor for the Next Generation of Phase-Change Materials