Comparison of structural and magnetic properties of Zn{sub x}Mg{sub 1.5-x}Mn{sub 0.5}FeO{sub 4} and MgAl{sub x}Cr{sub x}Fe{sub 2-2x}O{sub 4} spinel oxides
- Department of Physics, Saurashtra University, Rajkot-360005 (India)
The spinel oxides Zn{sub x}Mg{sub 1.5-x}Mn{sub 0.5}FeO{sub 4} (x = 0.0 to 0.6) and MgAl{sub x}Cr{sub x}Fe{sub 2-2x}O{sub 4} (x = 0.0 to 0.6) abbreviated as ZMMFO and MACFO respectively, were synthesized by standard ceramic processing. The compositional purity of all the specimens was checked by EDAX technique. The X-ray diffractometry was employed to determine the lattice constants and distribution of cations in the interstitial voids. The initial decrease of cell edge parameter (a) for ZMMFO up to x = 0.2 and thereafter expected rise in the ‘a’ and the initial slower rate of reduction in the lattice constant for MACFO are explained as basic of cation occupancy. The magnetic ordering in both systems is explained by invoking statistical canting models. The compositional variation of magneton number (n{sub B}) for ZMMFO could be very well explained by Localized canting of spin (LCS) model while Random canting of spin (RCS) model was used for MACFO system.
- OSTI ID:
- 22608855
- Journal Information:
- AIP Conference Proceedings, Vol. 1731, Issue 1; Conference: DAE solid state physics symposium 2015, Uttar Pradesh (India), 21-25 Dec 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electrical properties of MgAl{sub 2-2x}Zr{sub x}M{sub x}O{sub 4} (M = Co, Ni and x = 0.00-0.20) synthesized by coprecipitation technique using urea
Structural and magnetic properties of nanocrystalline Bi{sub 1-x}La{sub x}FeO{sub 3} (0.0 ≤ x ≤ 0.4) synthesized by a mechanochemical route
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ALUMINIUM COMPOUNDS
CERAMICS
CHROMIUM COMPOUNDS
COMPARATIVE EVALUATIONS
DISTRIBUTION
FERRITES
IMPURITIES
LATTICE PARAMETERS
MAGNESIUM COMPOUNDS
MAGNETIC PROPERTIES
MAGNETIZATION
MANGANESE COMPOUNDS
OXIDES
RANDOMNESS
SPIN
SPINELS
VOIDS
X-RAY DIFFRACTION
ZINC COMPOUNDS